Complaint
| Product Description | |
| Injection molding, Medium viscosity, High toughness at low temperature | |
| General | |
| Form Resin Pellets | |
| Feature Low Temperature Impact F1 Medium Viscosity | |
| Uses Telecommunications | |
| Physical Nominal Value Test Method | |
| Density / Specific Gravity(23 °C) 1.19 g/cm³ ISO 1183 | |
| Melt Viscosity(300 °C;1.0e+3 s-1) 600 Pa. s ISO 11443-A | |
| Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 10 cm³/10 min ISO 1133 | |
| Molding shrinkage, parallel(60x60x2;500 bar) 0.72 % ISO 2577 | |
| Molding shrinkage, normal(60x60x2;500 bar) 0.68 % ISO 2577 | |
| Mechanical Nominal Value Test Method | |
| Tensile Modulus(1 mm/min;23 °C) 2200 MPa ISO 527-1/-2 | |
| Tensile Stress, Yield(5 mm/min;23 °C) 60.0 MPa ISO 527-1/-2 | |
| Tensile Stress, Break(5 mm/min;23 °C) 70.0 MPa ISO 527-1/-2 | |
| Tensile Strain, Yield(5 mm/min;23 °C) 5.5 % ISO 527-1/-2 | |
| Tensile Strain, Break(5 mm/min;23 °C) 150 % ISO 527-1/-2 | |
| Flexural Modulus(2 mm/min;23 °C) 2300 MPa ISO 178 | |
| Flexural Stress(2 mm/min;23 °C) 90.0 MPa ISO 178 | |
| Notched Izod Impact Strength ISO 7391 | |
| 23 °C;3 mm 70 kJ/m² | |
| -20 °C;3 mm 60 kJ/m² | |
| -30 °C;3 mm 60 kJ/m² | |
| -40 °C;3 mm 60 kJ/m² | |
| Thermal Nominal Value Test Method | |
| Vicat Softening Temperature(120 °C/h;50 N) 136 °C ISO 306 | |
| Flame Rating UL 94 | |
| 1.5 mm V-0 | |
| 2 mm 5VB | |
| 2.5 mm 5VB | |
| Processing | Nominal Value |
| Drying Temperature - Dry Air Dryer<Injection> | 100 °C |
| Drying Time - Dry Air Dryer<Injection> | 4.0 hr |
| Mold Temperature<Injection> | 80 °C |
| Standard Melt Temperature<Injection> | 280 - 300 °C |