Complaint
| Product Description | ||
| LNP ELCRIN WF006XiQ compound is based on Poly butylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 37% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. Added features of this grade include: Excellent Strength, Stiffness and Dimensional Stability. Potential applications may include handles, connectors. | ||
| General | ||
| Form Resin Pellets | ||
| Filler 30 % Glass Fiber | ||
| Feature | Good Dimensional Pcr | Good Hardness 37 % Pcr |
| Uses | Automotive Electrical | Connector Consumer |
| Physical Nominal Value Test Method | ||
| Density / Specific Gravity 1.54 ASTM D792 1.54 g/cm³ ISO 1183 | ||
| Water Absorption | ||
| 24 hrs;23 °C 0.1 % ASTM D570 | ||
| 23 °C;saturated 0.09 % ISO 62-1 | ||
| Mold Shrinkage, Flow(3.2 mm) 0.5 - 0.7 % SABIC Method | ||
| Mold Shrinkage, XFlow(3.2 mm) 0.8 - 1 % SABIC Method | ||
| Melt Flow Rate[MFR](250 °C;5 kgf) 52 g/10min ASTM D1238 | ||
| Moisture Absorption(50% RH;23 °C) 0.1 % ISO 62 | ||
| Melt Volume Rate, MVR(5 kg;MVR at 250 °C) 38 cm³/10 min ISO 1133 | ||
| Mechanical | Nominal Value | Test Method |
| Izod Impact, Unnotched(23 °C) | 770 J/m | ASTM D4812 |
| Izod Impact, Notched | ||
| 23 °C | 82 J/m | ASTM D256 |
| -30 °C | 83 J/m | ASTM D256 |
| 80*10*4;23 °C | 8 kJ/m² | ISO 180/1A |
| 80*10*4;-30 °C | 8 kJ/m² | ISO 180/1A |
| Instrumented Dart Impact, Total Energy(23 °C) | 7 J | ASTM D3763 |
| C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 14 kJ/m² | ISO 179 1eA |
| Tensile Stress, Yield | ||
| 5 mm/min;Type I | 114 MPa | ASTM D638 |
| 5 mm/min | 139 MPa | ISO 527 |
| Tensile Stress, Break | ||
| 5 mm/min;Type I | 114 MPa | ASTM D638 |
| 5 mm/min | 139 MPa | ISO 527 |
| Tensile Strain, Yield | ||
| 5 mm/min;Type I | 2.2 % | ASTM D638 |
| 5 mm/min | 1.6 % | ISO 527 |
| Tensile Strain, Break | ||
| 5 mm/min;Type I | 2.2 % | ASTM D638 |
| 5 mm/min | 1.6 % | ISO 527 |
| Tensile Modulus | ||
| 5 mm/min | 1.2E+04 MPa | ASTM D638 |
| 1 mm/min | 1.1E+04 MPa | ISO 527 |
| Flexural Stress, Yield | ||
| 1.3 mm/min;50 mm;span | 210 MPa | ASTM D790 |
| 2 mm/min | 210 MPa | ISO 178 |
| Flexural Stress, break(1.3 mm/min;50 mm;span) | 189 MPa | ASTM D790 |
| Flexural Modulus | ||
| 1.3 mm/min;50 mm;span | 9100 MPa | ASTM D790 |
| 2 mm/min | 9100 MPa | ISO 178 |
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm | 203 °C 207 °C | ASTM D648 |
| CTE, Flow | ||
| -40 - 40 °C | 2.5e-05 1/°C | ASTM E831 |
| -40 - 40 °C | 2.5e-05 1/°C | ISO 11359-2 |
| CTE, XFlow | ||
| -40 - 40 °C | 8.9e-05 1/°C | ASTM E831 |
| -40 - 40 °C | 8.9e-05 1/°C | ISO 11359-2 |
| Ball Pressure Test, Approximate Maximum | 200 °C | IEC 60695-10-2 |
| HDT/Bf(0.45) | 217 °C | ISO 75/Bf |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | > 1E+15 ohms ·cm | ASTM D257 |
| Dielectric Strength, in Air(3.2 mm) | 23 kV/mm | ASTM D149 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 120 °C | |
| Drying Time<Injection> | 3 - 4 hrs | |
| Drying Time, Cumulative<Injection> | 12 hrs | |
| Maximum Moisture Content<Injection> | 0.02 % | |
| Melt Temperature<Injection> | 250 - 265 °C | |
| Nozzle Temperature<Injection> | 245 - 265 °C | |
| Front, Zone 3 Temperature<Injection> | 250 - 265 °C | |
| Middle, Zone 2 Temperature<Injection> | 245 - 260 °C | |
| Rear, Zone 1 Temperature<Injection> | 240 - 255 °C | |
| Mold Temperature<Injection> | 65 - 90 °C | |
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |
| Screw Speed <Injection> | 50 - 80 rpm | |
| Shot To Cylinder Size<Injection> | 40 - 80 % | |
| Vent Depth <Injection> | 0.025 - 0.038 mm |