Complaint
| Product Description | ||||
| Description Heat resistance, High Flow, High Impact. Application Automotive (Interior), E&E(housing) | ||||
| General | ||||
| Form | Resin Pellets | |||
| Feature | Good Thermal | Excellent Processability High Impact | ||
| UL Yellow Card E67171-100093014 | ||||
| Uses | Automotive Housing | Automotive Exterior Electrical | Automotive Interior | |
| Physical Nominal Value | Test Method | |||
| Density / Specific Gravity 1.14 g/cm³ | ASTM D792 | |||
| Melt Mass-Flow Rate, MFR(250 °C;2.16 kg) 5.3 g/10min | ASTM D1238 | |||
| Molding Shrinkage - Flow, Injection Molded(23 °C;3.2 mm) | 0.50 - 0.80 % | ASTM D955 | ||
| Mechanical Nominal Value | Test Method | |||
| Tensile Strength, Yield, Injection molded(50 mm/min;23 56.9 MPa °C;3.2 mm) | ASTM D638 | |||
| Tensile Elongation, Break, Injection Molded(50 mm/min;23 °C;3.2 mm) | > 100 % | ASTM D638 | ||
| Flexural Modulus, Injection Molded(10 mm/min;23 °C;3.22110 MPa mm) | ASTM D790 | |||
| Flexural Strength, Injection Molded(10 mm/min;23 °C;3.277.5 MPa mm;Span) | ASTM D790 | |||
| Notched Izod Impact, Injection Molded -30 °C;3.2 mm 23 °C;3.2 mm | 490 J/m 640 J/m | ASTM D256 | ||
| Thermal Nominal Value | Test Method | |||
| Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa;6.4 mm) | 113 °C | ASTM D648 | ||
| RTI Elec 60.0 °C | UL 746 | |||
| RTI Imp 60.0 °C | UL 746 | |||
| RTI Str 60.0 °C | UL 746 | |||
| Flame Rating 1.6 mm 3 mm | HB HB | UL 94 | ||