Higlue PC 9313 HIGH IMPACT WEARING COMPOUND

Higlue PC 9313, known as HIGH IMPACT WEARING COMPOUND, is a rubber modified epoxy with impact resistance recommended for lining and protecting.
Higlue PC 9313 is a grey, 2-part, rubber modified epoxy. With impact resistance superior to ceramic tile, it is recommended for lining and protecting flumes, troughs, elbows, hoppers, discharge chutes, and other processing equipment that is exposed to both abrasion and impact under typical temperatures of -20°F to +250°F (-29°C to +121°C).

* Cures to ceramic hardness - resists sliding abrasive wear
* Won't sag or shrink - conforms to overhead and irregular surfaces, application versatility
* Renews worn surfaces fast - reduces downtime
* Impact resistant - resists mild impact at 45° angles
* Offers the wear resistance properties of an epoxy along with impact resistance
* Trowelable

Ceramic Filled Epoxy/ Corrosion Repair Wearing Compounds

Ceramic beads filled epoxy repair putty is made up of high performance wear resistant and wear resistant ceramic particles and modified toughening and heat-resistant resin.

Ceramic beads wear resistant epoxy coating is widely used in repairing all kinds of wear parts and preparing wear-resistant and corrosion-resistant coatings on the surface of all kinds of machine parts. For example: repair and pre-protection of pipeline, elbow, mud pump, sand pump, centrifuge, packing box, slurry circulating pump body, impeller, size head of power plant desulfurization system, etc.

Features:

1. Ceramic-filled for outstanding resistance to abrasion;
2. Renews worn surfaces fast-reduces downtime;
3. Extends wear life- resists sliding abrasive wear and eliminates costly wear part inventory;
4. Non sag- provides abrasion resistance on over-head and vertical surfaces.

Ceramic Repair Putty

* Renews worn surfaces fast and reduces
* Downtime to put equipment back in service
* Quickly Easy to mix and use
* Non-sag paste allows application
* Versatility for overhead& vertical surfaces
* Non-shrinking
* Extends wear life
* Resists sliding abrasive wear
* Eliminates costly wear part
* Inventory Can be re-applied to
* itself Contains ceramic beads 1-1.5mm.

Technical Information

Application method	Trowel
Applications	Protective Coating
Compressive strength, ASTM-D695	12000.0 psi (83.0 N/mm² )
Cure type	Room Temperature (Ambient) Cure, Two Component Mix
Key characteristics	Impact Resistant, Prolongs Equipment Life, Renews Worn Surfaces, Sag: Non-Sag, Shrinkage: Non-Shrinking, Wear Resistant
Number of components	2 Part
Physical form	Paste
Recommended for use with	Metal
Mixed
Color, Mixed	Gray
Resin
Color, Resin	Gray
Hardener
Color, Hardener	Dark Gray

Product Type	Ceramic Repair Putty/ Abrasion Resistant Coating/ Wear Resistant Epoxy
Resistant Properties	Corrosion-Resistant
Pear Dia.	1- 1.5mm (can be customized)
Color	Grey (can be customized)
Mix Ratio by weight	8:1
Mix Ratio by volume	4:1
Working temperature	149ºC
Package Weight	30 lb per kit
working time	45-65 mins
Compressive strength(GB/T1041):	112.0MPa
Tensile strength(GB/T6329):	32.0MPa
Shear strength(GB/T7124):	14.0MPa
Flexural strength(GB/T9341):	45.0MPa
Fully curing time	16-24 hours
Shelf Life	12 month

Application

1. Cyclone and separator bodies
2. Dust collectors and exhausters
3. Pump liners and impellers
4. Fan blades and housings
5. Chutes and hoppers
6. Elbows and transition points

How to use

1. Surface treatment:
roughening the parts to be treated, sanding or sandblasting with an angle grinder, etc.; cleaning the roughened surface; the treated surface should be a rough and dry fresh substrate surface, and should be No oil and dust.

2. Preparation:
Mix the components A and B of the small particle wear-resistant protective agent according to the mass ratio A:B=2:1, and use them within 30 minutes.

3. Coating:
apply the uniformly mixed small particles of wear-resistant protective agent layer by layer to the area to be repaired, preferably at a thickness of 3-10 mm. The adhesive layer should be compacted to fully infiltrate the substrate; after the coating is applied to the required size, the surface layer is smoothed.

4. Curing:
Curing at 25ºC for 16 hours can be put into use. When the temperature is lower than 10 degrees, it can be cured by baking with an iodine tungsten lamp or electric heating plate for 2 hours.