| Product Description | |||
| Features: High Impact Strength Applications: Kitchen Appliances; Audio Supplies; Toilet Seats; Washing Machines; Vacuum Cleaner Housings and Tool Handle Accessories | |||
| General | |||
| Form | Resin Pellets | ||
| Feature High Impact Medium Impact Resistance | |||
| Tool Uses Washingmachine controlpanel | Kitchenware Audio Speaker Components | Vacuum cleaner | |
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity(23 °C) | 1.04 g/cm³ | ISO 1183 | |
| Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 17 cm³/10 min | ISO 1133 | |
| Molding Shrinkage | 0.40 - 0.70 % | ISO 294-4 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Strength, Yield(50 mm/min) | 44.0 MPa | ISO 527-2/50 | |
| Tensile Strength, Break(50 mm/min) | 33.0 MPa | ISO 527-2/50 | |
| Tensile Elongation, Break(50 mm/min) | 80 % | ISO 527-2/50 | |
| Flexural Modulus(2 mm/min) | 1900 MPa | ISO 178 | |
| Flexural Strength(2 mm/min) | 69.0 MPa | ISO 178 | |
| Charpy Notched Impact Strength | ISO 179 | ||
| -30 °C | 13 kJ/m² | ||
| 23 °C | 27 kJ/m² | ||
| Notched Izod Impact | ISO 180/1A | ||
| -30 °C | 12 kJ/m² | ||
| 23 °C | 25 kJ/m² | ||
| Thermal | Nominal Value | Test Method | |
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 82.0 °C | ISO 75-2/A | |
| Deflection Temperature Under Load, Annealed(1.8 MPa) 97.0 °C | ISO 75-2/A | ||
| Vicat Softening Temperature | |||
| 5 kg;50 ºC/hr | 98.0 °C | ISO 306/B50 | |
| 1kg;50ºC/hr | 103 °C | ISO 306/A50 | |
| CLTE, Flow | 8.8E-5 cm/cm/°C | ISO 11359-2 | |
| Flame Rating(1.5 mm) | HB | UL 94 | |
| Processing | Nominal Value |
| Drying Temperature<Injection> | 80 - 85 °C |
| Drying Time<Injection> | 2.0 - 4.0 hr |
| Rear Temperature<Injection> | 180 - 220 °C |
| Middle Temperature<injection> | 190 - 230 °C |
| Front Temperature<Injection> | 190 - 230 °C |
| Mold Temperature<Injection> | 30 - 70 °C |