| Jet Black Extrusion Grade Application: tubular products CHARACTERISTICS: Extrusion molding, Super high impact, High rigid | |||
| General | |||
| Form | Resin Pellets | ||
| Feature High Impact | High Mechanical Strength Ec 1907/2006 (Reach) And Rigidity | ||
| Uses | Tubing | ||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity(23 °C) | 1.05 g/cm³ | ASTM D792 | |
| Melt Mass-Flow Rate, MFR(220 °C;10 kg) | 5.7 g/10min | ASTM D1238 | |
| Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.70 % | ASTM D955 | |
| Rockwell Hardness, R-Scale(23 °C) | 96 | ASTM D785 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Strength(23 °C) | 36.0 MPa | ASTM D638 | |
| Flexural Modulus(23 °C) | 1960 MPa | ASTM D790 | |
| Flexural Strength(23 °C) | 62.0 MPa | ASTM D790 | |
| Notched Izod Impact(23 °C;6.35 mm) | 410 J/m | ASTM D256 | |
| Thermal | Nominal Value | Test Method | |
| Deflection Temperature Under Load, Unannealed(1.8 MPa;6.35 mm;bar 0) | 86.0 °C | ASTM D648 | |
| Deflection Temperature Under Load, Annealed(1.8 MPa;80 °C;8 hr) | 96.0 °C | ASTM D648 | |
| Vicat Softening Temperature(10 N;Loading 1) | 106 °C | ASTM D1525 | |
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||