| LNP FARADEX AS002 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 10% stainless steel fiber. Added features of this grade include: Electrically Conductive, EMI/RFI shielding. | ||||
| General | ||||
| Form | Resin Pellets | |||
| Filler 10 % Stainless Steel Fiber | ||||
| Feature Electrically Conductive Emi/Rfi Shielding | ||||
| Consumer Electrical | Packaging | Industria | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.12 g/cm³ 1.11 g/cm³ | ASTM D792 ISO 1183 | ||
| Moisture Absorption(23 °C;50% RH/24 hrs) | 0.2 % | ASTM D570 | ||
| Mold Shrinkage, Flow 24 hrs 24 hrs | 0.18 % 0.18 % | ASTM D955 ISO 294 | ||
| Mold Shrinkage, XFlow 24 hrs 24 hrs | 0.27 % 0.27 % | ASTM D955 ISO 294 | ||
| Mechanical | Nominal Value | Test Method |
| Izod Impact, Unnotched 23 °C 80*10*4;23 °C | 286 J/m 20 kJ/m² | ASTM D4812 ISO 180/1U |
| Izod Impact, Notched 23 °C 80*10*4;23 °C | 58 J/m 7 kJ/m² | ASTM D256 ISO 180/1A |
| Instrumented Dart Impact, Energy at Peak(23 °C) | 11 J | ASTM D3763 |
| Tensile Stress, Yield | 42 MPa | ASTM D638 |
| 39 MPa | ISO 527 | |
| Tensile Stress, Break | 39 MPa | ASTM D638 |
| 37 MPa | ISO 527 | |
| Tensile Strain, Yield | 2.2 % | ASTM D638 |
| 2.2 % | ISO 527 | |
| Tensile Strain, Break | 8.6 % | ASTM D638 |
| 3.3 % | ISO 527 | |
| Tensile Modulus 50 mm/min 1 mm/min | 2990 MPa 2500 MPa | ASTM D638 ISO 527 |
| Flexural Stress | 75 MPa | ASTM D790 |
| 66 MPa | ISO 178 | |
| Flexural Modulus | 2810 MPa | ASTM D790 |
| 2500 MPa | ISO 178 |
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 97 °C 87 °C | ASTM D648 |
| CTE, Flow -40 - 40 °C -40 - 40 °C | 7.9e-05 1/°C 7.8E-05 1/°C | ASTM E831 ISO 11359-2 |
| CTE, XFlow -40 - 40 °C -40 - 40 °C | 7.6E-05 1/°C 9.6E-05 1/°C | ASTM E831 ISO 11359-2 |
| HDT/Bf(0.45) | 91 °C | ISO 75/Bf |
| HDT/Af(1.8) | 78 °C | ISO 75/Af |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | 100 - 1.0E+06 ohms·cm | ASTM D257 |
| Surface Resistivity | 10 - 1.0E+05 ohms | ASTM D257 |
| Shielding Effectivness @ 3Mm | 40 - 55 dB | SABIC Method |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Drying Time<Injection> | 4 hrs | |
| Maximum Moisture Content<Injection> | 0.05 - 0.1 % | |
| Melt Temperature<Injection> | 240 - 255 °C | |
| Front, Zone 3 Temperature<Injection> | 255 - 265 °C | |
| Middle, Zone 2 Temperature<Injection> | 230 - 245 °C | |
| Rear, Zone 1 Temperature<Injection> | 210 - 220 °C | |
| Mold Temperature<Injection> | 70 - 95 °C | |
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |
| Screw Speed<Injection> | 30 - 60 rpm |
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||