| LUX9130T Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non- brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm / 5VA rating at 6.0mm and is UV stabilized providing additional weathering capability. LUX9130T is high transparency, extremly low haze and bubble free for thick part molding.LUX9130T is available in clear transparent and tinted color options that is an excellent candidate for a wide variety of applications. | ||||||
| General | ||||||
| Form | Resin Pellets | |||||
Feature | F1 Non-Chlorinated | High Clarity | Non-Brominated & Non- Chlorinated Flame Retardant | |||
| UL Yellow Card | E207780-101299184 | |||||
| Uses | Led Electrical | Healthcare | Light Guides | |||
| Physical | Nominal Value | Test Method | ||||
| Density / Specific Gravity | 1.19 1.2 g/cm³ | ASTM D792 ISO 1183 | ||||
| Mold Shrinkage, Flow(3.2 mm) | 0.45 - 0.65 % | SABIC Method | ||||
| Mold Shrinkage, XFlow(3.2 mm) | 0.5 - 0.7 % | SABIC Method | ||||
| Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | ||||
| Water Absorption(23 °C;saturated) | 0.1 % | ISO 62-1 | ||||
| Moisture Absorption(50% RH;23 °C) | 1.0E-02 % | ISO 62 | ||||
| Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | ||||
| UV light, water exposure/immersion | f1 | UL 746C | ||||
| Mechanical | Nominal Value | Test Method | ||||
| Izod Impact, Unnotched 23 °C -30 °C | NB J/m NB J/m | ASTM D4812 | ||||
| Izod Impact, Notched 23 °C -30 °C | 100 J/m 90 J/m | ASTM D256 | ||||
| Instrumented Dart Impact, Total Energy(23 °C) | 55 J | ASTM D3763 | ||||
| Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 | 130 kJ/m² 130 kJ/m² | ISO 180/1U | ||||
| Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 9 kJ/m² 9 kJ/m² | ISO 180/1A | ||||
| C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | 9 kJ/m² 9 kJ/m² | ISO 179 1eA | ||||
| C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | NB kJ/m² NB kJ/m² | ISO 179 1eU | ||||
| Tensile Stress, Yield | ||||||
| 50 mm/min;Type I | 64 MPa | ASTM D638 | ||||
| 50 mm/min | 64 MPa | ISO 527 | ||||
| Tensile Stress, Break | ||||||
| 50 mm/min;Type I | 59 MPa | ASTM D638 | ||||
| 50 mm/min | 50 MPa | ISO 527 | ||||
| Tensile Strain, Yield | ||||||
| 50 mm/min;Type I | 6 % | ASTM D638 | ||||
| 50 mm/min | 6 % | ISO 527 | ||||
| Tensile Strain, Break | ||||||
| 50 mm/min;Type I | 72 % | ASTM D638 | ||||
| 50 mm/min | 52 % | ISO 527 | ||||
| Tensile Modulus | ||||||
| 50 mm/min | 2370 MPa | ASTM D638 | ||||
| 1 mm/min | 2400 MPa | ISO 527 | ||||
| Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 98 MPa | ASTM D790 | ||||
| Flexural Modulus | ||||||
| 1.3 mm/min;50 mm;span | 2300 MPa | ASTM D790 | ||||
| 2 mm/min | 2410 MPa | ISO 178 | ||||
| Thermal | Nominal Value | Test Method |
| UL Recognized ≥ 6 mm ≥ 1.5 mm ≥ 0.4 mm | 5VA V-0 V-2 | UL 94 |
| Glow Wire Ignition Temperature [GWIT](1.5 mm) | 850 °C | IEC 60695-2-13 |
| Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 |
| Vicat Softening Temperature | ||
| Rate B/50 | 137 °C | ASTM D1525 |
| Rate B/50 | 137 °C | ISO 306 |
| Rate B/120 | 139 °C | ISO 306 |
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 131 °C 120 °C | ASTM D648 |
| CTE, Flow | ||
| -40 - 40 °C | 7.1e-05 1/°C | ASTM E831 |
| 23°C to 80°C | 7.4E-05 1/°C | ISO 11359-2 |
| CTE, XFlow | ||
| -40 - 40 °C | 7.1e-05 1/°C | ASTM E831 |
| 23°C to 80°C | 8.0e-05 1/°C | ISO 11359-2 |
| Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
| HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa) | 131 °C | ISO 75/Be |
| Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm) | 120 °C | ISO 75/Ae |
| Relative Temp Index, Elec | 125 °C | UL 746B |
| Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
| Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B |
| Electrical | Nominal Value | Test Method |
| Dielectric Constant, Dk(1.1e+9 Hz) | 2.81 | ASTM ES 7-83 |
| Dissipation Factor, Df(1.1e+9 Hz) | 5.8E-03 | ASTM ES 7-83 |
| Comparative Tracking Index, CTI | PLC 2 | UL 746A |
| Hot-wire Ignition, HWI ≥ 1.5 mm ≥ 0.4 mm | PLC 1 PLC 3 | UL 746A |
| High Amp Arc Ignition, HAI ≥ 6 mm ≥ 0.4 mm | PLC 0 PLC 1 | UL 746A |
| Optical | Nominal Value | Test Method |
| Light Transmission At 6.0 Mm(6 mm) | > 88 % | ASTM D1003 |
| Light Transmission At 1.0 Mm(1 mm) | > 90.5 % | SABIC Method |
| Light Transmission At 2.0 Mm(2 mm) | > 90 % | SABIC Method |
| Light Transmission At 3.0 Mm(3 mm) | > 89.5 % | SABIC Method |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 120 °C | |
| Drying Time<Injection> | 3 - 4 hrs | |
| Drying Time, Cumulative<Injection> | 48 hrs | |
| Maximum Moisture Content<Injection> | 0.02 % | |
| Melt Temperature<Injection> | 290 - 310 °C | |
| Nozzle Temperature<Injection> | 280 - 305 °C | |
| Front, Zone 3 Temperature<Injection> | 290 - 310 °C | |
| Middle, Zone 2 Temperature<Injection> | 275 - 300 °C | |
| Rear, Zone 1 Temperature<Injection> | 265 - 290 °C | |
| Mold Temperature<Injection> | 70 - 95 °C | |
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |
| Screw Speed <Injection> | 40 - 70 rpm | |
| Shot To Cylinder Size<Injection> | 40 - 60 % | |
| Vent Depth <Injection> | 0.025 - 0.076 mm |