| Classification: General grade. Characteristic: high flow Application: ABS Compounding ,ABS/PC Compounding,Cups,cosmetic container, Blower fan, pencil case, juicer, stereo dust cover&etc | ||||
| General | ||||
| Form Resin Pellets | ||||
| Feature Excellent Processability | ||||
| Compounding | Cups | Consumer | ||
| Uses Electrical | Containers | Stationary Supplies | ||
| White Goods & Small A li | ||||
| pp ances | ||||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.04 g/cm³ | ASTM D792 | ||
| Melt Mass-Flow Rate, MFR(220 °C;10 kg) | 28 - 32 g/10min | ASTM D1238 | ||
| Molding Shrinkage, Flow | 0.20 - 0.60 % | ASTM D955 | ||
| Water Absorption(24 hr) | 0.30 % | ASTM D570 | ||
| Rockwell Hardness, M-Scale | > 81 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield(50 mm/min;23 °C) | > 60.8 MPa | ASTM D638 | ||
| Flexural Modulus(2.8 mm/min;23 °C) | > 3040 MPa | ASTM D790 | ||
| Flexural Strength(2.8 mm/min;23 °C) | > 65.7 MPa | ASTM D790 | ||
| Notched Izod Impact Strength(6.4 mm) | > 2.0 kJ/m² | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | > 88.0 °C | ASTM D648 | ||
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | > 98.0 °C | ASTM D1525 | ||
| Flame Rating(3.2 mm) | HB | UL 94 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 80 - 85 °C | |||
| Drying Time<Injection> | 3.0 hr | |||
| Suggested Max Moisture<Injection> | < 0.10 % | |||
| Rear Temperature<Injection> | 190 - 200 °C | |||
| Middle Temperature<injection> | 200 - 220 °C | |||
| Front Temperature<Injection> | 210 - 220 °C | |||
| Nozzle Temperature<Injection> | 215 - 225 °C | |||
| Processing Temp, Melt<Injection> | 230 °C | |||
| Mold Temperature<Injection> | 60 - 80 °C | |||
| Injection Rate<Injection>A | Slow-Moderate | |||