Complaint
| Product Description |
| PC/ABS low gloss. |
| General |
| Form Resin Pellets |
| Feature Low Gloss Outdoor |
| UL Yellow Card E207780-523226 |
| Appliances Lighting Applications Automotive Lighting |
| Uses Electronic Displays Automotive Automotive Exterior |
| Automotive Interior Constraction Household Applications |
| Physical Nominal Value Test Method |
| Density / Specific Gravity 1.13 g/cm³ ASTM D792 |
| Melt Mass-Flow Rate, MFR(260 °C;5 kg) 17 g/10min ASTM D1238 |
| Molding Shrinkage, Across Flow(3.2 mm) 0.50 - 0.70 % Internal Method |
| Molding Shrinkage, Flow(3.2 mm) 0.50 - 0.70 % Internal Method |
| Water Absorption(24 hr) 0.10 % ASTM D570 |
| Water Absorption, Equilibrium(23 °C) 0.40 % ASTM D570 |
| Rockwell Hardness, R-Scale 118 ASTM D785 |
| Mechanical Nominal Value Test Method |
| Tensile Strength, Yield(50 mm/min;Type I) 54.0 MPa ASTM D638 |
| Tensile Elongation, Break(50 mm/min;Type I) 75 % ASTM D638 |
| Flexural Modulus(1.3 mm/min;50 mm;Span) 2300 MPa ASTM D790 |
| Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 84.0 MPa ASTM D790 |
| Notched Izod Impact ASTM D256 |
| -30 °C 320 J/m |
| 23 °C 530 J/m |
| Instrumented Dart Impact, Total Energy ASTM D3763 |
| -30 °C 33.0 J |
| 23 °C 40.0 J |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm | 123 °C 129 °C 107 °C 110 °C | ASTM D648 |
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 129 °C | ASTM D1525 |
| CLTE, Flow(-20 - 150 °C) | 7.2E-5 cm/cm/°C | ASTM E831 |
| CLTE, Transverse(-20 - 150 °C) | 7.2E-5 cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.20 W/m-K | ASTM C177 |
| RTI Elec | 60.0 °C | UL 746 |
| RTI Imp | 60.0 °C | UL 746 |
| RTI Str | 60.0 °C | UL 746 |
| Flame Rating(1.5 mm) | HB | UL 94 |
| Electrical | Nominal Value | Test Method |
| Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 |
| Comparative Tracking Index[CTI] | PLC 2 | UL 746 |
| High Amp Arc Ignition, HAI, Surface | PLC 0 | UL 746 |
| Hot-wire Ignition, HWI | PLC 2 | UL 746 |
| Optical | Nominal Value | Test Method |
| Gardner Gloss, Untextured(60°) | 30 | ASTM D523 |
| Processing | Nominal Value |
| Drying Temperature<Injection> | 105 - 110 °C |
| Drying Time<Injection> | 3.0 - 4.0 hr |
| Suggested Max Moisture<Injection> | 0.040 % |
| Suggested Shot Size<Injection> | 30 - 80 % |
| Rear Temperature<Injection> | 250 - 290 °C |
| Middle Temperature<injection> | 255 - 295 °C |
| Front Temperature<Injection> | 260 - 300 °C |
| Nozzle Temperature<Injection> | 275 - 300 °C |
| Processing Temp, Melt<Injection> | 275 - 300 °C |
| Mold Temperature<Injection> | 60 - 90 °C |
| Back Pressure<Injection> | 0.300 - 0.700 MPa |
| Screw Speed <Injection> | 40 - 70 rpm |
| Vent Depth <Injection> | 0.038 - 0.076 mm |
| Drying Time, Cumulative<Injection> | 8 hrs |