| CCP PBT PBT-4115 Application: Connectors, cooling fans, sockets, coil shafts, engine parts, switches, television parts, rectifiers Characteristic: Containing 15% glass fiber, high strength, flammability grade up to 1/32inch, UL94-V0, easy to form | ||
| General | ||
| Form Resin Pellets | ||
| Filler 15 % Glass Fiber | ||
| Feature High Strength Excellent Processability | ||
| Uses | Automotive Industry (interior And Body Parts) | Connector Switches Electron & electric parts Socket |
| Physical Nominal Value Test Method | ||
| Density / Specific Gravity 1.47 - 1.56 g/cm³ ASTM D792 | ||
| Moisture Absorption(24 h) 0.03 % ASTM D570 | ||
| Molding Shrinkage, Flow 0.3 - 0.6 % ASTM D955 | ||
| Molding Shrinkage, Across Flow 1.2 - 1.8 % ASTM D955 | ||
| Hardness, Rockwell, M-scale 93 ASTM D785 | ||
| Mechanical Nominal Value Test Method | ||
| Tensile Strength 88 - 108 MPa ASTM D638 | ||
| Tensile Elongation 2.5 - 4.5 % ASTM D638 | ||
| Flexural Strength 118 - 167 MPa ASTM D790 | ||
| Flexural Elongation ≥ 4413 MPa ASTM D790 | ||
| Izod impact strength, Notched(6.35 mm;bar 0) 39 - 69 J/m ASTM D256 | ||
| Thermal Nominal Value Test Method | ||
| Melting Point 225 °C DSC | ||
| Heat Deflection Temperature ASTM D648 | ||
| 1.82 MPa 205 °C | ||
| 0.45 MPa 220 °C | ||
| CLTE, Flow 5.5E-5 cm/cm/°C ASTM D696 | ||
| Flammability(0.8 mm) V-0 UL 94 | ||
| Electrical | Nominal Value | Test Method |
| Dielectric Constant(60 Hz) | 3.3 | ASTM D150 |
| Dissipation Factor(60 Hz) | 0.001 | ASTM D150 |
| Volume Resistivity | > 1.0E+15 ohms ·cm | ASTM D257 |
| Surface Resistance | > 1.0E+13 ohms | ASTM D257 |
| Dielectric Strength(2 mm) | > 20 KV/mm | ASTM D149 |
| Arc Resistance | 90 sec | ASTM D495 |