Complaint
| Product Description | |||
| Features: High Gloss; Ultra High Rigidity; Good Tensile Strength Applications: Phone Cases; Lamp Holders; Toys; Office Supplies; Clock Cases and Home Appliance Buttons High Stiffness | |||
| General | |||
| Form | Resin Pellets | ||
| Feature | High Mechanical Strength High Reflection And Rigidity Good Stretchability | Good Hardness | |
| Light Covers | Toys | Household electric | |
| Uses | product,etc. | ||
| Electrical applications | Office supplies | Telephone | |
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity(23 °C) | 1.06 g/cm³ | ISO 1183 | |
| Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 20 cm³/10 min | ISO 1133 | |
| Molding Shrinkage | 0.40 - 0.70 % | ISO 294-4 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Strength, Yield(50 mm/min) | 50.0 MPa | ISO 527-2/50 | |
| Tensile Strength, Break(50 mm/min) | 36.0 MPa | ISO 527-2/50 | |
| Tensile Elongation, Break(50 mm/min) | 60 % | ISO 527-2/50 | |
| Flexural Modulus(2 mm/min) | 2300 MPa | ISO 178 | |
| Flexural Strength(2 mm/min) | 79.0 MPa | ISO 178 | |
| Charpy Notched Impact Strength | ISO 179 | ||
| -30 °C | 8.0 kJ/m² | ||
| 23 °C | 14 kJ/m² | ||
| Notched Izod Impact | ISO 180/1A | ||
| -30 °C | 7.0 kJ/m² | ||
| 23 °C | 13 kJ/m² | ||
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 83.0 °C | ISO 75-2/A |
| Deflection Temperature Under Load, Annealed(1.8 MPa) | 98.0 °C | ISO 75-2/A |
| Vicat Softening Temperature | ||
| 5 kg;50 ºC/hr | 100 °C | ISO 306/B50 |
| 50 ºC/hr;1 kg | 104 °C | ISO 306/A50 |
| CLTE, Flow | 8.4E-5 | ISO 11359-2 |
| Flame Rating(1.5 mm) | HB | UL 94 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 - 85 °C | |
| Drying Time<Injection> | 2.0 - 4.0 hr | |
| Rear Temperature<Injection> | 180 - 220 °C | |
| Middle Temperature<injection> | 190 - 230 °C | |
| Front Temperature<Injection> | 190 - 230 °C | |
| Mold Temperature<Injection> | 30 - 70 °C |