Complaint
| Product Description | |||
| Features: High flow; good paint finish; easy to make large molded parts Application: Paintable two-wheeler applications | |||
| General | |||
| Form | Resin Pellets | ||
| Feature Good Adhesion Excellent Processability | |||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity(23 °C) | 1.04 g/cm³ | ISO 1183 | |
| Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 50 cm³/10 min | ISO 1133 | |
| Molding Shrinkage | 0.40 - 0.70 % | ISO 294-4 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Stress, Yield(50 mm/min) | 41.0 MPa | ISO 527-2/50 | |
| Tensile Stress, Break(50 mm/min) | 30.0 MPa | ISO 527-2/50 | |
| Tensile Strain, Break(50 mm/min) | 70 % | ISO 527-2/50 | |
| Flexural Modulus(2 mm/min) | 2100 MPa | ISO 178 | |
| Flexural Stress(2 mm/min) | 61.0 MPa | ISO 178 | |
| Charpy Notched Impact Strength(23 °C) | 20 kJ/m² | ISO 179 | |
| Notched Izod Impact Strength(23 °C) | 19 kJ/m² | ISO 180/1A | |
| Thermal | Nominal Value | Test Method | |
| Deflection Temperature Under Load, Annealed(1.8 | MPa) 96.0 °C | ISO 75-2/A | |
| Vicat Softening Temperature 5 kg;50 ºC/hr 50 ºC/hr;1 kg | 99.0 °C 104 °C | ISO 306/B50 ISO 306/A50 | |
| CLTE, Flow | 8.3E-5 cm/cm/°C | ISO 11359-2 | |
| Flame Rating(1.5 mm) | HB | UL 94 | |
| Processing | Nominal Value | ||
| Drying Temperature | 80 - 85 °C | ||
| Drying Time | 2 - 4 °C | ||
| Barrell Temperature - Front | 190 - 230 °C | ||
| Barrell Temperature - Middle | 190 - 230 °C | ||
| Barrell Temperature - Rear | 180 - 220 °C | ||
| Mold Temperature | 30 - 60 °C | ||