| Features: Chemical resistance; Vacuum forming; Refrigerator sheet Application: Refrigerator sheet | ||||
| General | ||||
| Form | ||||
| Feature | ||||
| UL Yellow Card E56070-550778 | ||||
| Uses Refrigerator interior | ||||
| Physical | Nominal Value | Test Method | ||
| Apparent Density, Bulk | 1.05 g/cm³ | ISO 60 | ||
| Melt Mass-Flow Rate, MFR(220 °C;10 kg) | 3.0 g/10min | ISO 1133 | ||
| Molding Shrinkage | 0.40 - 0.70 % | ISO 294-4 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Stress, Yield(50 mm/min) | 46.0 MPa | ISO 527-2/50 | ||
| Tensile Stress, Break(50 mm/min) | 35.0 MPa | ISO 527-2/50 | ||
| Tensile Elongation, Break(50 mm/min) | 25 % | ISO 527-2/50 | ||
| Flexural Modulus(2 mm/min) | 1800 MPa | ISO 178 | ||
| Flexural Strength(2 mm/min) | 63.0 MPa | ISO 178 | ||
| Charpy Notched Impact Strength -30 °C 23 °C | 24 kJ/m² 35 kJ/m² | ISO 179 | ||
| Notched Izod Impact -30 °C 23 °C | 22 kJ/m² 33 kJ/m² | ISO 180/1A | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 84.0 °C | ISO 75-2/A | ||
| Deflection Temperature Under Load, Annealed(1.8 MPa) | 100 °C | ISO 75-2/A | ||
| Vicat Softening Temperature 50 ºC/hr;1 kg 5 kg;50 ºC/hr | 106 °C 101 °C | ISO 306/A50 ISO 306/B50 | ||
| CLTE, Flow | 8.7E-5 | ISO 11359-2 | ||
| Flame Rating(1 mm) | HB | UL 94 | ||
| Processing | Nominal Value |
| Drying Temperature<Extrusion> | 80 - 85 °C |
| Drying Time<Extrusion> | 2.0 - 4.0 hr |
| Cylinder Zone 1 Temp. <Extrusion> | 190 - 210 °C |
| Cylinder Zone 3 Temp. <Extrusion> | 210 - 240 °C |
| Cylinder Zone 5 Temp. <Extrusion> | 220 - 250 °C |
| Die Temperature<Extrusion> | 200 - 250 °C |