Complaint
| Product Description | ||||
| Automotive: High heat resistance. Excellent flow/impact balance. High gloss. | ||||
| General | ||||
| Form | Resin Pellets | |||
| Feature | High Reflection | Good Thermal | ||
| Appliances Automotive Interior | Automotive | Automotive Exterior | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.04 g/cm³ | ASTM D792 | ||
| Melt Mass-Flow Rate, MFR 230 °C;3.8 kg 260 °C;5 kg 220 °C;10 kg | 3.5 g/10min 18 g/10min 10 g/10min | ASTM D1238 ASTM D1238 ISO 1133 | ||
| Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.80 % | Internal Method | ||
| Rockwell Hardness, R-Scale | 104 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method |
| Tensile Modulus | ||
| 5 mm/min | 2370 MPa 2350 MPa | ASTM D638 ISO 527-2/1 |
| Tensile Strength, Yield | ||
| 5 mm/min;Type I | 42.0 MPa 46.0 MPa | ASTM D638 ISO 527-2/50 |
| Tensile Strength, Break | ||
| 5 mm/min;Type I | 33.0 MPa 35.0 MPa | ASTM D638 ISO 527-2/50 |
| Tensile Elongation, Yield | ||
| 5 mm/min;Type I | 2.6 % 2.6 % | ASTM D638 ISO 527-2/50 |
| Tensile Elongation, Break | ||
| 5 mm/min;Type I | 27 % 18 % | ASTM D638 ISO 527-2/50 |
| Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min | 2290 MPa 2170 MPa | ASTM D790 ISO 178 |
| Flexural Stress, at Yield(2 mm/min) | 69.0 MPa | ISO 178 |
| Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 71.0 MPa | ASTM D790 |
| Charpy Notched Impact Strength -30 °C;80*10*4;sp=62mm 0 23 °C;80*10*4;sp=62mm 0 | 11 kJ/m² 25 kJ/m² | ISO 179 1eA |
| Notched Izod Impact | ||
| 23 °C | 300 J/m | ASTM D256 |
| 6.4 mm;23 °C | 240 J/m | ASTM D256 |
| 80*10*4 mm;-40 °C | 9.0 kJ/m² | ISO 180/1A |
| 80*10*4 mm;-30 °C | 10 kJ/m² | ISO 180/1A |
| 80*10*4 mm;23 °C | 25 kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 99.0 °C 86.0 °C 93.0 °C 85.0 °C | ASTM D648 ASTM D648 ASTM D648 ISO 75-2/Af |
| Vicat Softening Temperature | 104 °C 106 °C | ISO 306/B50 ISO 306/B120 |
| RTI Elec | 60.0 °C | UL 746 |
| RTI Imp | 60.0 °C | UL 746 |
| RTI Str | 60.0 °C | UL 746 |
| Flame Rating(1.5 mm) | HB | UL 94 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 90 - 95 °C | |
| Drying Time<Injection> | 2.0 - 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.10 % | |
| Suggested Shot Size<Injection> | 50 - 70 % | |
| Rear Temperature<Injection> | 195 - 210 °C | |
| Middle Temperature<injection> | 210 - 225 °C | |
| Front Temperature<Injection> | 230 - 255 °C | |
| Nozzle Temperature<Injection> | 230 - 275 °C | |
| Processing Temp, Melt<Injection> | 230 - 275 °C | |
| Mold Temperature<Injection> | 50 - 80 °C | |
| Back Pressure<Injection> | 0.300 - 0.700 MPa | |
| Screw Speed<Injection> | 30 - 60 rpm | |
| Vent Depth<Injection> | 0.038 - 0.051 mm | |
| Drying Time, Cumulative<Injection> | 8 hrs |