| Test Method | Test Item | Result | |
| ISO 4892-2 | Xenon Arc Weathering | Non-exposure | 2000h Exposure |
| ISO 4892-2 | Color Change | - | Gray Scale 3 |
| ISO 178 | Flexural Strength Flexural Modulus | 26.3Mpa 2.44Gpa | 25.0 Mpa, decrease 4.9% 2.24GPa,decrease 8.2% |
| ISO 179 | Impact Strength | 4.86KJ/ | 4.66KJ/,decrease 4.1% |
| Test Method | Characters | Result |
| ASTM D638 | Tensile test | 18.0Mpa |
| ASTM E831 | Coefficient of linear thermal expansion | 40.5 μm/mC |
| ASTM D256 | Impact resistance | 33.7J/m Type of break: Complete Break |
| ASTM D6109 | Flexural strength | MOR:29.3Mpa MOE:3715Mpa |
| ASTM D790 | Flexural properties | MOR:34.1Mpa MOE:2503Mpa |
| ASTM D4060 | Abrasion resistance | Weight loss: 0.07g |
| ASTM D6007 | Formaldehyde test | ND² |
| Items | Co-extruded WPC | Normal WPC |
| Color: | Rich, vivid,strong steady leveling natural wood color | Single solid color and the very few thickness oxidation |
| Anti-scratch | Stronger | Better than wood |
| Expansion rate | Lower,about 0.1% | About 0.3-0.5% |
| Water absorption | Smaller only the two ends | Better than wood |
| Weathering test | Much stronger | Better than wood |
| Water/oil stain | N/A | May occasionally occur |
| Cleaning Method | Water, very easy | Sand paper,steel wool etc |
| Wood grain | Never disappears | May be not very clear |
| Mold stain | N/A | Better than wood |
| Country | Sales Quantity in 2017 |
| France | 1000sqm |
| Germany | 9700sqm |
| Australia | 4200sqm |
| Established | 2004 |
| Factory area: | 36,000 sqm |
| Workshop Area: | 30,000 sqm |
| Annual Turnover: | Average more than USD 10,000,000 |
| Production capacity : | 140 containers/Month |
| Mixed granulating lines: | 7 Domestic lines and 2 Germany lines |
| Extruding lines: | 42 Domestic lines and 5 Austria lines |
| Dealing face lines: | 8 Domestic lines and 1 Germany line |
| Wood grain lines: | 3Domestic Lines |
| Operator: | 128 |
| QC/Engineer: | 10/5 |
| International big projects: | 2008,2012,2016 Olympic Games |