Inlet manifold of automobile engine, radiator tank parts, motor cover, tire cover, tension wheel, cooling fan, jetting machine accessories, electronics, connection terminal, disconnector, bearing cage, power tools cover, high performance gear, coil skeleton, textile accessories and so on.
Tensile strength | MPa | ISO 527 | I type sample 50mm/min | 75 |
Elongation at break | % | ISO 527 | I type sample 50mm/min Gauge length 50mm | 20 |
Flexural strength | MPa | ISO 178 | 23ºC 10mm/min | 90 |
Flexural modulus | MPa | ISO 178 | 23ºC 10mm/min | 2800 |
Izod impact strength(notched) | KJ/m2 | ISO 180 | 23ºC | 4 |
Charpy impact strength(unnotched) | KJ/m2 | ISO 179 | 23ºC | NB |
Melting point | ºC | ISO 11357-1 | 220 | |
HDT | ºC | ISO 75 | 0.45MPA | 170 |
1.8MPA | 65 |
UL Flammability | Class | UL-94 | HB | |
GWIT | IEC60695-2-13 |
1.Packing:
In 25kg PP woven bag, or per your requirement.
17-20mt/20'FCL 24-28mt/40'FCL
2.Storage:
The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air.
3.Transportation:
During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.