80 kg/m3 is a popular density.
UTEK PVC foam is a cross-linked rigid structural PVC foam material, as a close cell foam, based on vinyl polymer, modified with the throughout Aramids link. It is the compounding chemical material based on PVC and PUR. It is said as the cross-linked PVC foam core, in the international practice.It can be used as the core material in the sandwich structure.
| Item | Standard | Unit | P45 | P60 | P80 | P100 | P130 | P200 | |
| Density | ISO 845 | Kg/m3 | msmv | 45 | 60 | 80 | 100 | 130 | 200 |
| Density(Nominal) | ISO 845 | Kg/m3 | msv | / | 54 | 72 | / | / | / |
| Tensile strength | ASTM C297 | Mpa | msv | 1.4 | 1.8 | 2.5 | 3.5 | 4.5 | 7.1 |
| Tensile strength | ASTM C297 | Mpa | msmv | 1.1 | 1.5 | 2.2 | 2.5 | 3.5 | 6.3 |
| Tensile modulus | ASTM C297 | Mpa | msv | 55 | 75 | 95 | 130 | 175 | 250 |
| Tensile modulus | ASTM C297 | Mpa | msmv | 45 | 57 | 85 | 105 | 135 | 210 |
| Compressive strength | ISO 844 | Mpa | msv | 0.6 | 0.93 | 1.4 | 2 | 3 | 4.8 |
| Compressive strength | ISO 844 | Mpa | msmv | 0.5 | 0.7 | 1.15 | 1.65 | 2.4 | 4.2 |
| Compressive modulus | ISO 844 | Mpa | msv | 50 | 70 | 90 | 135 | 170 | 240 |
| Compressive modulus | ISO 844 | Mpa | msmv | 45 | 60 | 80 | 115 | 145 | 200 |
| Shear strength | ISO 1922 | Mpa | msv | 0.5 | 0.76 | 1.15 | 1.44 | 2.1 | 3.5 |
| Shear strength | ISO 1922 | Mpa | msmv | 0.46 | 0.63 | 0.95 | 1.4 | 1.9 | 3.2 |
| Shear modulus | ISO 1922 | Mpa | msv | 15 | 20 | 27 | 35 | 50 | 85 |
| Shear modulus | ISO 1922 | Mpa | msmv | 12 | 16 | 23 | 28 | 40 | 75 |
| Shear elongation,at break | ISO 1922 | % | msmv | 8 | 10 | 15 | 15 | 20 | 20 |
| Shear elongation,at break | ISO 1922 | % | msv | / | 20 | 30 | / | / | / |