POM raw material or modified reinforced for industrial products and toys, textile industry
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | |||
| Hostaform® MT® SlideXTM2404 is a low melt viscosity injection molding grade for fast cycling and thin walled parts with tribological modification designed for use in demanding applications that require prevention of audible noise caused by stick-slip phenomenon and low friction and wear against plastics and metals. Hostaform® MT SlideXTM 2404 is a special grade developed for medical industry applications and complies with: CFR 21 (177.2470) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 11559) and the Device Master File (MAF 1079) the corresponding EU and national registry regulatory requirements biocompatibility in tests corresponding to USP <88> Class VI/ISO 10993 low residual monomers no animal- derived constituents | |||
| General | |||
| Form | Resin Pellets | ||
| Biocompatible Medium-Low Viscosity Excellent Processability | |||
| Feature | No Animal Derived Dmf 11559 Fda | ||
| Components Maf | |||
| Uses | Thin-walled Parts Medical | ||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.40 g/cm³ | ISO 1183 | |
| Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 25 cm³/10 min | ISO 1133 | |
| Molding Shrinkage, Across Flow | 1.8 % | ISO 294-4 | |
| Molding Shrinkage, Flow | 1.9 % | ISO 294-4 | |
| Water Absorption, Saturation(23 °C) | 0.60 % | ISO 62 | |
| Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | |
| Ball Indentation Hardness(30s) | 130 MPa | ISO 2039-1 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Modulus | 2550 MPa | ISO 527-2/1A | |
| Tensile Stress, Yield | 55.0 MPa | ISO 527-2/1A/50 | |
| Tensile Strain, Yield | 7.0 % | ISO 527-2/1A/50 | |
| Nominal Tensile Strain at Break | 50 % | ISO 527-2/1A/50 | |
| Flexural Modulus(23 °C) | 2300 MPa | ISO 178 | |
| Charpy Notched Impact Strength | ISO 179 1eA | ||
| -30 °C | 5.5 kJ/m² | ||
| 23 °C | 5.5 kJ/m² | ||
| Charpy Unnotched Impact Strength | ISO 179 1eU | ||
| -30 °C | 150 kJ/m² | ||
| 23 °C | 160 kJ/m² | ||
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature, Unannealed(1.8 MPa) | 90.0 °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 °C | ISO 306/B50 |
| Melting Point(10 °C/min) | 166 °C | ISO 11357-3 |
| CLTE, Flow | 1.4E-4 cm/cm/°C | ISO 11359-2 |
| CLTE, Transverse | 1.4E-4 cm/cm/°C | ISO 11359-2 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 100 - 120 °C | |
| Drying Time<Injection> | 3.0 - 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.15 % | |
| Hopper Temperature<Injection> | 20 - 30 °C | |
| Rear Temperature<Injection> | 170 - 175 °C | |
| Middle Temperature<injection> | 180 - 185 °C | |
| Front Temperature<Injection> | 180 - 195 °C | |
| Nozzle Temperature<Injection> | 190 - 200 °C | |
| Processing Temp, Melt<Injection> | 180 - 200 °C | |
| Mold Temperature<Injection> | 80 - 120 °C | |
| Injection Rate<Injection> | Slow-Moderate | |
| Back Pressure<Injection> | < 4.00 MPa | |
| Feeding Zone Temperature<Injection> | 60 - 80 °C | |
| Zone4 temperature<Injection> | 180 - 200 °C | |
| Hot Runner Temperature<Injection> | 190 - 200 °C |
Forever Co.,Ltd
ITEM NO: PC XH-25W-34
FEATURE:Light Shielding Polycarbonate,Injection Molding Grade,
Flammability Rating UL-94 V-0(1.0mm) /5VA(2.5mm),
Weathering Rating UL746C F1 grade,with ordinary shading effect,
good low temperature resistance, good fluidity,
excellent molding performance, in line with environmental protection requirements
| TYPICAL PROPERTIES | STANDARD | UNIT | TYPICAL VALUE | |
| Physical Property | Specific Gravity | ISO1183 | g/cm3 | 1.23 |
| Melt Flow Rate(300ºC 1.2kg) | ISO1133 | g/10min | 11 | |
| Water Absorption | ISO62 | % | 0.25 | |
| Mechanical Property | Tensile Strength(50mm/min) | ISO527 | MPa | 55 |
| Elongation at break(50mm/min) | ISO527 | % | 60 | |
| Tensile Strength(50mm/min) | ISO527 | MPa | 2000 | |
| Flexural Strength(2mm/min) | ISO178 | MPa | 90 | |
| Flexural Modulus(2mm/min) | ISO178 | 2100 | 2100 | |
| Notched Charpy Impact Strength(23ºC) | ISO180 | KJ/m2 | 50 | |
| Notched Charpy Impact Strength(-35ºC/3H) | ISO180 | KJ/m2 | 30 | |
| Thermal Property | HDT (1.8MPa) | ISO75 | ºC | 120 |
| Linear expansion coefficient | ASTM D696 | ×10-5cm/cm/ºC | 7.0 | |
| Mold shrinkage | ASTM D955 | % | 0.5-0.7 | |
| Flammability | UL94 | -- | V0(1.0mm) 5VA(2.5mm) | |
| RTI | Elec | UL746B | ºC | 130(1.0mm) |
| Imp | UL746B | ºC | 125(1.0mm) | |
| Str | UL746B | ºC | 130(1.0mm) | |
| UV | Weather Resistance | UL746C | F1 or F2 | F1 |