| General Purpose Grade Application: heel, toy, clock shell, audio shell, suitcase, plate products CHARACTERISTICS: High impact resistance | ||||
| General | ||||
| Form | Resin Pellets | |||
| Feature | High Impact Ec 1907/2006 (Reach) | |||
| UL Yellow Card E162823-224713 | ||||
| Uses | Extrusion Of Profiles And Tote Box Sheets | Housing Toys | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity(23 °C) | 1.04 g/cm³ | ASTM D792 | ||
| Melt Mass-Flow Rate, MFR | ASTM D1238 | |||
| 200 °C;5 kg | 1.6 g/10min | |||
| 220 °C;10 kg | 22 g/10min | |||
| Rockwell Hardness, R-Scale(23 °C) | 105 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength(23 °C) | 41.0 MPa | ASTM D638 | ||
| Flexural Modulus(23 °C) | 2350 MPa | ASTM D790 | ||
| Flexural Strength(23 °C) | 73.0 MPa | ASTM D790 | ||
| Notched Izod Impact(23 °C;6.35 mm) | 310 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Under Load, Unannealed(1.8 MPa;12.7 mm) | 85.0 °C | ASTM D648 | ||
| Deflection Temperature Under Load, Annealed(1.8 MPa;80 °C;8 hr) | 95.0 °C | ASTM D648 | ||
| Vicat Softening Temperature(10 N;Loading 1) | 102 °C | ASTM D1525 | ||
| Flame Rating, all color | UL 94 | |||
| 1.5 mm | HB | |||
| 3 mm | HB | |||
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||