| CCP PBT PBT-5115 Characteristic: Halogen free | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | 15 % Glass Fiber | ||
| Non Brominated & Non | |||
| Feature | Chlorinated Flame | ||
| Physical | Nominal Value | Test Method | |
| Specific Gravity | 1.40 - 1.46 g/cm³ | ASTM D792 | |
| Moisture Absorption(24 h) | 0.03 % | ASTM D570 | |
| Molding Shrinkage, Flow | 0.1 - 0.5 % | ASTM D955 | |
| Molding Shrinkage, Across Flow | 0.8 - 1.3 % | ASTM D955 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Strength | 78 - 98 MPa | ASTM D638 | |
| Tensile Elongation | 2.5 - 4.5 % | ASTM D638 | |
| Flexural Strength | 127 - 157 MPa | ASTM D790 | |
| Flexural Elongation | ≥ 4903 MPa | ASTM D790 | |
| Izod impact strength, Notched(6.35 mm;bar 0) | 39 - 69 J/m | ASTM D256 | |
| Hardness, Rockwell, M-scale | 85 - 90 | ASTM D785 | |
| Thermal | Nominal Value | Test Method | |
| Melting Point | 225 °C | DSC | |
| Heat Deflection Temperature | ASTM D648 | ||
| 1.82 MPa | 185 °C | ||
| 0.45 MPa | 205 °C | ||
| CLTE, Flow | 5E-5 cm/cm/°C | ASTM D696 | |
| Flammability(0.8 mm) | V-0 | UL 94 | |
| Electrical | Nominal Value | Test Method |
| Dielectric Constant(60 Hz) | 3 | ASTM D150 |
| Dissipation Factor(60 Hz) | 0.01 | ASTM D150 |
| Volume Resistivity | > 1.0E+15 ohms·cm | ASTM D257 |
| Surface Resistance | > 1.0E+13 ohms | ASTM D257 |
| Dielectric Strength(2 mm) | > 19 KV/mm | ASTM D149 |
| Arc Resistance | 120 sec | ASTM D495 |