| CCP PBT PBT-4830 Application: Connectors, cooling fans, sockets, coil shafts, engine parts, switches, television parts, rectifiers Characteristic: Containing 30% glass fiber, High strength, Good heat resistance, flammability grade up to 1/8inch, UL94-V0 | ||||||
| General | ||||||
| Form | Resin Pellets | |||||
| Filler | 30 % Glass Fiber | |||||
| Feature | Good Thermal High Strength | |||||
| Uses | Automotive Industry (interior And Body Parts) | Connector | Switches Socket | |||
| Electron & electric parts | ||||||
| Physical | Nominal Value | Test Method | ||||
| Specific Gravity | 1.55 - 1.65 g/cm³ | ASTM D792 | ||||
| Moisture Absorption(24 h) | 0.03 % | ASTM D570 | ||||
| Molding Shrinkage, Flow | 0.2 - 0.5 % | ASTM D955 | ||||
| Molding Shrinkage, Across Flow | 0.8 - 1.4 % | ASTM D955 | ||||
| Mechanical | Nominal Value | Test Method | ||||
| Tensile Strength | 98 - 137 MPa | ASTM D638 | ||||
| Tensile Elongation | 2.5 - 4.5 % | ASTM D638 | ||||
| Flexural Strength | 147 - 226 MPa | ASTM D790 | ||||
| Flexural Elongation | ≥ 6865 MPa | ASTM D790 | ||||
| Izod impact strength, Notched(6.35 mm;bar 0) | 69 - 108 J/m | ASTM D256 | ||||
| Hardness, Rockwell, M-scale | 94 | ASTM D785 | ||||
| Thermal | Nominal Value | Test Method | ||||
| Melting Point | 225 °C | DSC | ||||
| Heat Deflection Temperature | ASTM D648 | |||||
| 1.82 MPa | 205 °C | |||||
| 0.45 MPa | 220 °C | |||||
| CLTE, Flow | 3E-5 cm/cm/°C | ASTM D696 | ||||
| Flammability(3 mm) | V-0 | UL 94 | ||||
| Electrical | Nominal Value | Test Method |
| Dielectric Constant(60 Hz) | 3.5 | ASTM D150 |
| Dissipation Factor(60 Hz) | 0.001 | ASTM D150 |
| Volume Resistivity | > 1.0E+15 ohms·cm | ASTM D257 |
| Surface Resistance | > 1.0E+13 ohms | ASTM D257 |
| Dielectric Strength(2 mm) | > 20 KV/mm | ASTM D149 |
| Arc Resistance | 100 sec | ASTM D495 |