304 Stainless Steel Flat Bar, is for all applications where greater strength and superior corrosion resistance is required. 304 Stainless Steel Flat Bar has a durable dull, grainy mill finish and is widely used for all types of fabrication projects that are exposed to the elements.
Frame work, braces, supports, plates, marine, food, etc.
ASTM A276 Standard Specification for Stainless Steel Bars and Shapes.
3mm*10mm-30mm*180mm.
| ASTM | JIS | GB |
|---|---|---|
| 304 | SUS 304 | 06Cr19Ni10 |
| Steel Grade | C | Si | Mn | P | S | Cr | Ni | N |
|---|---|---|---|---|---|---|---|---|
| 304 | 0.08 max | 1.00 max | 2.0 max | 0.045 max | 0.030 max | 18.0-20.0 | 8.0-11.0 | / |
| 304L | 0.03 max | 1.00 max | 2.0 max | 0.045 max | 0.030 max | 18.0-20.0 | 8.0-12.0 | / |
| 304N | 0.08 max | 1.00 max | 2.0 max | 0.045 max | 0.030 max | 18.0-20.0 | 8.0-11.0 | 0.10-0.16 |
| Steel Grade | Delivery Condition | Thickness | Tensile Strength (Mpa) | Yield Strength (Mpa) | Elongation in 2 in. (50 mm) | Reduction of Area |
|---|---|---|---|---|---|---|
| 304 | Annealed | 12.7mm max | 620 Mpa min | 310 Mpa min | 30% min | 40% min |
| 304 | Annealed | 12.7mm min | 515 Mpa min | 205 Mpa min | 30% min | 40% min |
| 304L | Annealed | 12.7mm max | 620 Mpa min | 310 Mpa min | 30% min | 40% min |
| 304L | Annealed | 12.7mm min | 485 Mpa min | 170 Mpa min | 30% min | 40% min |
| 304N | Annealed | Whole Sizes | 550 Mpa min | 240 Mpa min | 30% min | / |
| 304/304L/304N | Relatively severe cold work | 19.5mm max | 860 Mpa min | 690 Mpa min | 12% min | 35% min |
| 304/304L/304N | Relatively severe cold work | 19.5mm - 25.4mm | 795 Mpa min | 550 Mpa min | 15% min | 35% min |
| 304/304L/304N | Relatively severe cold work | 25.4mm - 31.75mm | 690 Mpa min | 345 Mpa min | 24% min | 45% min |
| 304/304L/304N | Strain Hardened | 50.8mm max | 650 Mpa min | 515 Mpa min | 25% min | 40% min |
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.