TDS OF LC-FEP | |||
Name of indicators | Unit | Value | Test Method |
Relative density | g/cm 3 | 2.12-2.18 | ASTM D792 |
Melt flow rate | g/10min | customizable | ASTM D1238 |
Melting point | ºC | 270±5 | GB/T 16582 |
Tensile strength | MPa | ≥18 | ASTM D638 |
Elongation at break | % | ≥275 | ASTM D638 |
Hardeness | Shore hardness | 58 | ASTM D2240 |
Yield strength | MPa | - | - |
Dynamic friction coefficient | - | 0.3 | GB/T 10006 |
Maximal Temperature of Continuous Work | ºC | 200 | - |
Heat distortion temperature | ºC(1.82MPa) | 47 | GB/T 19466 |
Thermal expansion Coefficient | (-10 -5 /ºC) | 8-15 | ASTM D696 |
Volume resistivity | Ω.cm | 10 16-10 18 | ASTM D257 |
Insulation breakdown Voltage | KV(3.2mm) | 20 | ASTM D149 |
Relative dielectric Constant | 10 3Hz | 2.1-2.3 | ASTM D150 |
Dielectric loss angle tangent | 10 6Hz | <0.0005 | ASTM D150 |
Note: The above data is the representative value of our self -test, which is not applicable to the only basis for formulating specifications or as designed. |