Item | Carbon fiber prepreg |
Material | epoxy resin+carbon cloth |
curing temperature | Low temperature(80ºC) & Medium temperature(120ºC-130ºC) |
curing time | 120-180min |
Storage life at -5ºC | 6Months |
Storage life at -18ºC | 12Months |
Resin | 20-45% |
Type | Yarn | Weave | Density(10mm) | Weight(g/m2) | Thickness(mm) | Width(cm) | ||
Warp | Weft | Warp | Weft | |||||
01P-100 | 1k | 1k | plain | 7.5 | 7.5 | 100 | 0.14 | 100-150 |
01T-100 | 1k | 1k | twill | 7.5 | 7.5 | 100 | 0.14 | 100-150 |
01P-120 | 1k | 1k | plain | 9 | 9 | 120 | 0.16 | 100-150 |
01T-120 | 1k | 1k | twill | 9 | 9 | 120 | 0.16 | 100-150 |
01P-140 | 1k | 1k | plain | 10.5 | 10.5 | 140 | 0.17 | 100-150 |
01T-140 | 1k | 1k | twill | 10.5 | 10.5 | 140 | 0.17 | 100-150 |
01E-140 | 1k | 1k | Satin | 12 | 12 | 160 | 0.18 | 100-150 |
03P-180 | 3k | 3k | plain | 4.5 | 4.5 | 180 | 0.28 | 100-150 |
03T-180 | 3k | 3k | twill | 4.5 | 4.5 | 180 | 0.28 | 100-150 |
03P-200 | 3k | 3k | plain | 5 | 5 | 200 | 0.3 | 100-150 |
03T-200 | 3k | 3k | twill | 5 | 5 | 200 | 0.3 | 100-150 |
03P-240 | 3k | 3k | plain | 6 | 6 | 240 | 0.32 | 100-150 |
03T-240 | 3k | 3k | twill | 6 | 6 | 240 | 0.32 | 100-150 |
03P-280 | 3k | 3k | plain | 7 | 7 | 280 | 0.34 | 100-150 |
03T-280 | 3k | 3k | twill | 7 | 7 | 280 | 0.34 | 100-150 |
03E-320 | 3k | 3k | Satin | 8 | 8 | 320 | 0.36 | 100-150 |
06P-280 | 6k | 6k | plain | 3.5 | 3.5 | 280 | 0.36 | 100-150 |
06T-280 | 6k | 6k | twill | 3.5 | 3.5 | 280 | 0.36 | 100-150 |
06P-320 | 6k | 6k | plain | 4 | 4 | 320 | 0.38 | 100-150 |
06T-320 | 6k | 6k | twill | 4 | 4 | 320 | 0.38 | 100-150 |
06P-400 | 6k | 6k | plain | 5 | 5 | 400 | 0.42 | 100-150 |
06T-400 | 6k | 6k | twill | 5 | 5 | 400 | 0.42 | 100-150 |
12P-400 | 12k | 12k | plain | 2.5 | 2.5 | 400 | 0.46 | 100-150 |
12T-400 | 12k | 12k | twill | 2.5 | 2.5 | 400 | 0.46 | 100-150 |
12P-480 | 12k | 12k | plain | 3 | 3 | 480 | 0.52 | 100-150 |
12T-480 | 12k | 12k | twill | 3 | 3 | 480 | 0.52 | 100-150 |
12P-640 | 12k | 12k | plain | 4 | 4 | 640 | 0.64 | 100-150 |
12T-640 | 12k | 12k | twill | 4 | 4 | 640 | 0.64 | 100-150 |