| Free-flowing, rapidly solidifying grade with increased stiffness and heat distortion resistance. Highly stabilized to resist aggressive fuels including hot diesel fuel. | |||
| General | |||
| Form | Resin Pellets | ||
| Fuel Resistant Excellent Processability Enhanced Stiffness Ec 1907/2006 (Reach) | |||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.41 g/cm³ | ISO 1183 | |
| Apparent Density, Bulk | 0.85 g/cm³ | No Standard | |
| Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 11 cm³/10 min | ISO 1133 | |
| Molding Shrinkage, Across Flow | 2.1 % | ISO 294-4 | |
| Molding Shrinkage, Flow | 2.1 % | ISO 294-4 | |
| Water Absorption, Saturation(23 °C) | 0.80 % | ISO 62 | |
| Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | |
| Ball Indentation Hardness(H 358/30) | 155 MPa | ISO 2039-1 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Modulus | 3000 MPa | ISO 527-2 | |
| Tensile Stress, Yield | 66.0 MPa | ISO 527-2/50 | |
| Tensile Strain, Yield | 9.0 % | ISO 527-2/50 | |
| Nominal Tensile Strain at Break | 30 % | ISO 527-2/50 | |
| Tensile creep modulus(1000 hr;5%;23 °C;strain < = 0) | 1450 MPa | ISO 899-1 | |
| Charpy Notched Impact Strength | ISO 179 1eA | ||
| -30 °C | 5.5 kJ/m² | ||
| 23 °C | 5.5 kJ/m² | ||
| Charpy Unnotched Impact Strength | ISO 179 1eU | ||
| -30 °C | 170 kJ/m² | ||
| 23 °C | 170 kJ/m² | ||
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature, Unannealed(1.8 MPa) | 100 °C | ISO 75-2/A |
| Melting Point | 171 °C | ISO 11357-3 |
| CLTE, Flow(23 - 55 °C) | 1.1E-4 cm/cm/°C | ISO 11359-2 |
| Maximum Service Temperature - short cycle operation | 100 °C | |
| Flammability Classification(1.6 mm) | HB | IEC 60695-11-10/- 20 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | 1.0E+15 ohms | IEC 60093 |
| Volume Resistivity | 1.0e+14 ohms·cm | IEC 60093 |
| Electric Strength | 85 kV/mm | IEC 60243-1 |
| Relative Permittivity(1000000 Hz) | 3.70 | IEC 60250 |
| Dissipation Factor(1000000 Hz) | 5.0E-3 | IEC 60250 |
| Comparative Tracking Index, Solution A | 600 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 100 °C | |
| Drying Time<Injection> | 3.0 hr | |
| Suggested Max Moisture<Injection> | 0.20 % | |
| Hopper Temperature<Injection> | 200 °C | |
| Rear Temperature<Injection> | 200 °C | |
| Middle Temperature<injection> | 200 °C | |
| Front Temperature<Injection> | 200 °C | |
| Nozzle Temperature<Injection> | 200 °C | |
| Processing Temp, Melt<Injection> | 190 - 230 °C | |
| Mold Temperature<Injection> | 60 - 120 °C | |
| Residence Time<Injection> | < 10.0 min | |
| Screw Speed<Injection> | < 18 m/min |
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||