PVC resin is the most widely raw material used in plastic production. It has good chemical stability corrosion resistance and water resistance. It can be dissolved in ace-tones , hydrochloric ether, ester and some alcohol . It can offer good solubility , good electrical insulation , thermoplasticity and membrane forming capacity.
The PVC Resins are polymerized by suspension process, their appearance being in white powder form. They are essential materials for preparing PVC compounds. By adding blending agents and employing different techniques, they can be made into rigid or non-rigid PVC products and are suppliable in a wide range of transparent, translucent, and opaque colours.
Specifications:
Tape: | SG1 | SG2 | SG3 | SG4 | SG5 | SG6 | SG7 | SG8 |
K value | 77-75 | 74-73 | 72-71 | 70-69 | 68-66 | 65-63 | 62-60 | 59-55 |
Viscosity, ml/g | 156-144 | 143-136 | 135-127 | 126-119 | 118-107 | 106-96 | 95-87 | 86-73 |
Average polymerization |
|
| 1350-1250 | 1250-1150 | 1100-1000 | 950-850 | 950-850 | 750-650 |
Number of impurity particle max | 30 | 30 | 30 | 30 | 30 | 30 | 40 | 40 |
Volatiles content % max | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 |
Appearing density g/ml min | 0.42 | 0.42 | 0.42 | 0.42 | 0.42 | 0.45 | 0.45 | 0.45 |
Residual after sieve 0.25mm mesh max | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 |
0.063mm min | 90 | 90 | 90 | 90 | 90 | 90 | 90 | 90 |
Number of grain/400cm2 max | 40 | 40 | 40 | 40 | 40 | 40 | 40 | 40 |
Plasticizer absorbency value of 100g resin | 25 | 25 | 25 | 22 | 19 | 16 | 14 | 14 |
Whiteness % min | 74 | 74 | 74 | 74 | 74 | 74 | 70 | 70 |
Residual chlorethylenecontent mg/kg max | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 5 |
Etc mg/kg max | 150 | 150 | 150 | 150 | 150 | 150 | 150 | 150 |
Application:
PVC resin - SG3 K-Value 72-71, Average degree of polymerization 1350-1250
PVC resin - SG4 K-Value 70-69, Average degree of polymerization 1250-1150
PVC resin - SG5 K-Value 68-66, Average degree of polymerization 1100-1000
PVC resin - SG6 K-Value 65-63, Average degree of polymerization 950-850
PVC resin - SG7 K-Value 62-60, Average degree of polymerization 850-750
PVC resin - SG8 K-Value 59-55, Average degree of polymerization 750-650
SG-1 is used in producing high-grade electrical insulating material
SG-2 is used in producing electrical insulating material, common soft products and film
SG-3 is used in producing electrical insulating materials, agricultural film, daily-use plastic products,
SG-4 is used in producing membranelle for industrial and civil use, tube and pipes
SG-5 is used in producing transparent products section bar, hard tube and decorative materials
SG-6 is used in producing clear foil, hard board and welding rod
SG-7, SG-8 is used in producing clear foil, hard injection molding.
Packaging & Shipping:
Package:25kg/bag, PP valve bag with PE liner. 17MT/1x20ft container
Storage and transport: Prevent from rain, snow, humid, sunshine, throwing and other mechanical damage