Complaint
| Product Description | ||||
| Polypropylene copolymer reinforced with 30% chemically coupled glass fiber | ||||
| General | ||||
| Form | ||||
| Filler | ||||
| Feature | Ec 1907/2006 (Reach) Chemically Coupled | |||
| UL Yellow Card E477602-102433050 | ||||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.12 g/cm³ | ASTM D792 | ||
| Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 3.0 g/10min | ASTM D1238 | ||
| Molding Shrinkage | 0.30 % | No Standard | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 72.0 MPa | ASTM D638 | ||
| Tensile Elongation, Break | 3.0 % | ASTM D638 | ||
| Flexural Modulus | 5000 MPa | ASTM D790 | ||
| Notched Izod Impact(23 °C) | 150 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 145 °C | ASTM D648 | ||
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 120 °C | ASTM D1525 | ||
| Flame Rating 1.6 mm 3.2 mm | HB HB | UL 94 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 80 °C | |||
| Drying Time<Injection> | 2.0 hr | |||
| Rear Temperature<Injection> | 210 °C | |||
| Middle Temperature<injection> | 240 °C | |||
| Front Temperature<Injection> | 250 °C | |||
| Mold Temperature<Injection> | 50 - 70 °C | |||