| Product Description | |||
| PP copo Compound, 20% glass fibre reinforced, chemically coupled | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | 20 % Glass Fiber | ||
| Feature Chemically Coupled | |||
| Physical | Nominal Value | Test Method | |
| Density | 1.02 - 1.06 g/cm³ ISO 1183 | ||
| Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) 18 - 23 g/10min ISO 1133 | |||
| Ball Indentation Hardness(H 358/30) | 92.0 MPa | ISO 2039-1 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Stress | > 75.0 MPa | ISO 527-2 | |
| Tensile Strain, Break | > 3.0 % | ISO 527-2 | |
| Flexural Modulus | > 3200 MPa | ISO 178 | |
| Charpy Notched Impact Strength(23 °C) > 10 kJ/m² ISO 179 | |||
| Charpy Unnotched Impact Strength(23 °C) > 30 kJ/m² ISO 179 | |||
| Thermal | Nominal Value | Test Method | |
| Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa | 158 °C 144 °C | ISO 75-2/B ISO 75-2/A | |
| Glow Wire Ignition Temperature [GWIT] 1.6 mm 3.2 mm | 750 °C 750 °C | ||