- Unfilled PEEK granule
- 8200GB (PFLUON brand)
- Standard viscosity and flowability
- Suitable for injection, extrusion, compouding, and production of PEEK filament, fiber and film.
Technical Data Sheet
I. Basic Information
| Product name | Polyetheretherketone Resin |
| Product grade | 8200GB |
| Brand | PFLUON |
II. Specifications
| Properties | Test Standard | Test Conditions | Unit | Typical Value |
| Mechanical Properties | ||||
| Tensile Strength | ISO 527 | 23ºC | MPa | 98 |
| Tensile Strain at Break | ISO 527 | 23ºC | % | 28 |
| Tensile Modulus | ISO 527 | 23ºC | GPa | 3.5 |
| Flexural Strength | ISO 178 | 23ºC | MPa | 155 |
| Flexural Modulus | ISO 178 | 23ºC | GPa | 3.5 |
| Charpy Impact Strength | ISO 179/1eA | 23ºC | KJ/m2 | 7.0 |
| Thermal Properties | ||||
| Melting Point | ISO 11357 | DSC | ºC | 343 |
| Glass Transition Temp. | ISO 11357 | DSC | ºC | 150 |
| Other Properties | ||||
| Density | ISO 1183 | 23ºC | g/cm3 | 1.3 |
| Shore D Hardness | ISO 868 | 23ºC | - | 85 |
| Melt Volume Flow Rate | ISO 1133 | 380ºC, 5Kg | cm3/10min | 20 |
| Drying Temperature / Time | 150°C / 3h or 120°C / 5h (residual moisture <0.02%) |
| Temperature Settings | 355 / 360 / 365 / 370 / 375°C (Nozzle) |
| Hopper Temperature | Not greater than 100°C |
| Mould Temperature | 170°C - 200°C |
| Gate | >1mm or 0.5 x part thickness |
| Statement: This certificate has been prepared with care and the best of our knowledge as part of the testing system of ZHEJIANG PFLUON TECHNOLOGY CO., LTD. However, it does not relieve our customers of their obligation to inspect the goods upon receipt or establish any warranties to third parties, and it is only a reference to the general basic performance information of the product. The document issued electronically, valid without signature. |