Item No. | Viscosity (cps) | Mix Ratio (By weight) | Operating Time(25ºC /min) | Curing time (hr, basically cured) | Curing time (hr, perfectly cured) | Hardness (shore A) | Tear strength (kN/m) | Tensile strength (Mpa) | Elongation (%) |
INI-605 | 4500±500 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 5±2 | 9±2 | 2.3±0.5 | 410~510 |
INI-610 | 9000±3000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 10±2 | 14±2 | 3±1 | 350~450 |
INI-615 | 12000±2000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 15±2 | 18±2 | 3.5±0.5 | 390~460 |
INI-620 | 15000±1000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 20±2 | 21±3 | 4.4±0.5 | 405~500 |
INI-625 | 18000±2000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 25±2 | 26±5 | 4.2±0.5 | 455~520 |
INI-630 | 23000±5000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 30±2 | 28±5 | 5.6±0.5 | 420~510 |
INI-635 | 19000±5000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 35±2 | 25±4 | 5.2±0.5 | 260~410 |
INI-640 | 12000±5000 | 100 :2-100:4 | 30~50 | 3~5 | 12 | 38±2 | 21±4 | 5±0.5 | 190~360 |