Bucket White Inov 200kg Plastic Polyether with Factory Price Tdi

Min.Order: 1,000
Product origin: Zibo, Shandong, China
Infringement complaint: complaintComplaint
US$ 2.5 ~ 5.5

Description
Polyether/TDI type prepolymer
The products have good wear resistance, water resistance, mold resistance, excellent mechanical properties, and color can be added to adjust the color. It is used to make polyurethane products such as rubber stick, rubber wheel, plate, rubber coating and miscellaneous parts.
ModelD1140D1145D1155D1160D1180D1185
NCO/%4.0±0.24.5±0.25.5±0.26.0±0.28.0±0.28.5±0.2
State at 20 ºCColorless Transparent Liquid
MOCA
100g Prepolymer /g
11.513.016.017.52324.0
Viscosity (85ºC)/mPa·s340300250250450400
Mixing temperature /ºC(Prepolymer/MOCA)80/12080/12080/12080/12075/11075/110
Gel time /min109.59622
Post vulcanization time (100ºC) /h101010101010
Hardness(Shore A)78±282±288±192±1  
Hardness(Shore D)    70±178±1
100% Modulus/MPa4.65.05.56.223.232.5
300% Modulus /MPa8.29.213.020.8--
Tensile strength /MPa272832353942
Elongation / %550480400350230180
Tear strength /(KN/m)46557678123145
Rebound / %282424334051
Density (24ºC)/(g/ cm3)1.111.121.141.141.181.18
Din wear /mm³14811210914113189
ModelD1230D1235D1240D1245D1250D1262D1265D1270
NCO/%3.0±0.13.5±0.14.0±0.14.5±0.25.0±0.26.2±0.26.5±0.27.0±0.2
State at 20 ºCColorless Transparent Liquid
MOCA
100g Prepolymer /g
8.610.311.51314.5181920.5
Viscosity (85ºC)/mPa·s200250350400450240300400
Mixing temperature /ºC(Prepolymer/MOCA)85/12085/12080/12080/12080/12075/12075/12075/120
Gel time /min954.543.532.52
Post vulcanization time (100ºC) /h1010101010101010
Hardness(Shore A)70±278±284±286±290±194±197±1(53D)60D±1
100% Modulus/MPa2.14.25.45.98.99.215.215.8
300% Modulus /MPa3.06.310.010.314.616.824.623
Tensile strength /MPa710192131323533
Elongation / %600550500480460450440420
Tear strength /(KN/m)34445357737895120
Rebound / %5048413130314143
Density (24ºC)/(g/ cm3)1.081.091.111.131.141.151.161.17
Din wear /mm³163159116157135117143135.6

Why choose our company?
 1) be with good quality and pretty competitve price.
 2) improve the quality of your production, simplifying the processing method.
 3) customized and improve your competitiveness in your field.

Scroll to Top