Complaint
| Project | Test data | Data unit | ||
| Basic properties | Density | 0.920-0.923 | g/cm3 | |
| Melt flow rate | 2.1-2.9 | g/10min | ||
| Mechanical properties | Turbidity | ≤30 | % | |
| Tensile Strength | crosswise | ≥20 | N/mm | |
| length wise direction | ≥50 | N/mm | ||
| Cleanliness | ≤7 | Per/kg | ||
| Tensile breaking strength | ≥9 | Mpa | ||
| Elongation at break | ≥500 | % | ||
| Project | Test data | Data unit | |
| Basic properties | Density | 0.9205~0.9245 | g/cm3 |
| Melt flow rate | 1.7-2.3 | g/10min | |
| Mechanical properties | Elongation at break | ≥200 | % |
| Tensile strength at break | ≥17 | Mpa | |
| Tensile strength yield | ≥3.0 | ||
| Shore hardness | ≥44 | ||
| Thermal properties | Vicat softening point | ≥90 | ºC |
| Project | Test data | Data unit | |
| Basic properties | Density | 0.9205~0.9245 | g/cm3 |
| Melt flow rate | 1.7-2.3 | g/10min | |
| Mechanical properties | Elongation at break | ≥200 | % |
| Tensile strength at break | ≥17 | Mpa | |
| Tensile strength yield | ≥3.0 | ||
| Shore hardness | ≥44 | ||
| Thermal properties | Vicat softening point | ≥90 | ºC |
| Project | Test data | Data unit | |
| Basic properties | Density | 0.9205~0.9245 | g/cm3 |
| Melt flow rate | 1.7-2.3 | g/10min | |
| Mechanical properties | Elongation at break | ≥200 | % |
| Tensile strength at break | ≥17 | Mpa | |
| Tensile strength yield | ≥3.0 | ||
| Shore hardness | ≥44 | ||
| Thermal properties | Vicat softening point | ≥90 | ºC |