El modelo | 
Grosor | 
A[2856k] | 
D65 | 
La estabilidad química | 
ND | 
Α×10-7 | 
Tg | 
Ts | |||||

(Mm) | 
X | 
Y. | 
Y. | 
X | 
Y. | 
Y. | 
DA | 
DW | 
(/ºC) | 
(ºC) | 
(ºC) | ||

El HB600. | 
2 | 
0.68 | 
0.319 | 
27 | 
0.675 | 
0,325 | 
16.5 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB610 | 
2 | 
0.695 | 
0.305 | 
18.4 | 
0.69 | 
0.31 | 
10.7 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB630 | 
2 | 
0.713 | 
0.287 | 
10.4 | 
0.711 | 
0.289 | 
5.5 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB640 | 
2 | 
0.724 | 
0.276 | 
5 | 
0.723 | 
0.277 | 
2.4 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB650 | 
2 | 
0.728 | 
0.272 | 
3.2. | 
0.728 | 
0.272 | 
1.5 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB670 | 
2 | 
0.731 | 
0.269 | 
1.1. | 
0.73 | 
0.27 | 
0.5 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB685 | 
2 | 
0.734 | 
0,266 | 
0.3 | 
0.734 | 
0,266 | 
0.1 | 
1 | 
2 | 
1.523 | 
103 | 
527 | 
605 |

El HB700 | 
2 | 
0.735 | 
0.265 | 
0 | 
0.735 | 
0.265 | 
0 | 
1 | 
2 | 
1.523 | 
111 | 
534 | 
592 |

El HB720 | 
3 | 
 | 
 | 
 | 
 | 
 | 
 | 
5 | 
4 | 
1.532 | 
111 | 
534 | 
592 |

El modelo | 
Grosor | 
Λtj | 
Λ0 | 
Tλ0 | 
K | 
Bubbles | 
La banda |

(Mm) | 
(Nm). | 
(Nm). | 
(%) | ||||

El HB600. | 
2 | 
600 ± 10 | 
680 | 
≥ 88,7 | 
≥1,2 | 
C-B | 
3C |

El HB610 | 
2 | 
610 ± 10 | 
680 | 
≥ 88,7 | 
≥1,2 | 
C-B | 
3C |

El HB630 | 
2 | 
630 ± 10 | 
700 | 
≥ 88,7 | 
≥1,2 | 
C-B | 
3C |

El HB640 | 
2 | 
640 ± 10 | 
720. | 
≥ 88,7 | 
≥1,2 | 
C-B | 
3C |

El HB650 | 
2 | 
650 ± 10 | 
720. | 
≥ 87,5 | 
≥ 1.0 | 
C-B | 
3C |

El HB670 | 
2 | 
670 ± 10 | 
750 | 
≥ 87,5 | 
≥ 1.0 | 
C-B | 
3C |

El HB685 | 
2 | 
685 ± 10 | 
800 | 
≥ 83,6 | 
≥0,8 | 
C-B | 
3C |

El HB700 | 
2 | 
700 ± 10 | 
800 | 
≥ 79,8 | 
≥0,8 | 
C-B | 
3C |