| El tema | 1870dtex/2 (1680D/2) | 1400dtex/2 1.260 D/2 | 930 dtex/2 840D/2 | 2100dtex/2 (1890d/2) | 1170dtex/1 (1050D/1) | 700 dtex/1 (630D/1) | 1870dtex/1 (1680D/1) | 1400dtex/1 (1.260 D/1) | 930 dtex/1 (840D/1) | ||
| Resistencia a la ruptura≥ | N/final | 279.30 | 215.60 | 137.20 | 313.60 | 90.00 | 50.00 | 137.00 | 107.00 | 70.00 | |
| Alargamiento en | 88.2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
| 66,6N | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | ||
| 44.1N | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | ||
| Fuerza adhesiva≥ | N/cm. | 166.60 | 147.00 | 117.60 | 176.40 | 65.00 | 43.00 | 83.00 | 69.00 | 54.00 | |
| Resistencia a la ruptura diferencia≤ | % | 3.80 | 3.80 | 3.80 | 3.80 | 5.00 | 5.00 | 5.00 | 5.00 | 5.00 | |
| Rompiendo la elongación diferencia≤ | 6.30 | 6.30 | 6.30 | 6.30 | 7.00 | 7.50 | 7.00 | 7.00 | 7.00 | ||
| Recogida en el DIP | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | ||
| Rompiendo la elongación | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 | |
| De diámetro | Mm | 0,78±0,03 | 0,65±0,03 | 0,55±0,03 | 0,78±0,03 | - | 0,23±0,03 | 0.5±0.03 | 0,43±0,03 | 0,32±0,03 | |
| Twist | Giro principal(Z) | Trenzado/m | 320±15 | 370±15 | 460±15 | 320±15 | TPM/m: 200±15 | TPM/m: 260±15 | 160±10 | 190±10 | 210±15 |
| El segundo giro(S) | 320±15 | 370±15 | 460±15 | 320±15 | |||||||
| El encogimiento de calor ≤ | % | 6.00 | 6.00 | 6.00 | 4.00 | 4.50 | 4.00 | 4.00 | 4.00 | 4.00 | |
| La humedad ≤ | % | 1.00 | 1.00 | 1.00 | 1.00 | 0.80 | 0.80 | 0.80 | 0.80 | 0.80 | |
| NO. | Los elementos | UNITE | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
| (1100dtex/2) | (1440 dtex/2) | (1100dtex/3) | (1670dtex/2) | (2200dtex/2) | (1440 dtex/3) | (1670dtex/3) | ||||
| 1 | Romper Stength (min) | N/final | 140 | 180 | 205 | 205 | 280 | 260 | 305 | |
| 2 | Alargamiento a la 44.1N | % | 4.5+1.0 | |||||||
| Alargamiento a la 58.0N | % | 4.5+1.0 | ||||||||
| Alargamiento en 66,6N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Alargamiento a la 88.2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Alargamiento de 100N | % | 4.5+1.0 | ||||||||
| 3 | Adhension(H-test) (min) | N/cm. | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
| 4 | Resistencia a la ruptura diferencia(máx.). | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| 5 | Rompiendo la elongación diferencia(máx.). | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 6 | Recogida en el DIP | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
| 7 | Rompiendo la elongación (Min). | % | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | |
| 8 | De diámetro | Mm | 0.56+0.03 | 0.61+0.03 | 0.66+0.03 | 0.66+0.03 | 0.75+0.03 | 0.74+0.03 | 0.81+0.03 | |
| 9 | Twist | Pingle twist(Z) | T/10cm. | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 |
| Telas twist(S) | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 | |||
| 10 | El encogimiento de aire caliente a 177ºC×2minx0.05CN/dtex(máx.). | % | 3 | 3 | 3 | 3 | 3 | 3 | 3 | |
| 11 | @ De elongación de la rotura de hilo de trama (Min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 | |
| NO. | Los elementos | UNITE | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
| (1100dtex/2) | (1440 dtex/2) | (1100dtex/3) | (1670dtex/2) | (2200dtex/2) | (1440 dtex/3) | (1670dtex/3) | ||||
| 1 | Romper Stength (min) | N/final | 140 | 180 | 205 | 205 | 270 | 260 | 305 | |
| 2 | Alargamiento a la 44.1N | % | 4.5+1.0 | |||||||
| Alargamiento a la 58.0N | 4.5+1.0 | |||||||||
| Alargamiento en 66,6N | 4.5+1.0 | 4.5+1.0 | ||||||||
| Alargamiento a la 88.2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Alargamiento de 100N | % | 4.5+1.0 | ||||||||
| 3 | Adhension(H-test) (min) | N/cm. | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
| 4 | Resistencia a la ruptura diferencia(máx.). | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| 5 | Rompiendo la elongación diferencia(máx.). | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 6 | Recogida en el DIP | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
| 7 | Rompiendo la elongación (min) | % | 14 | 14 | 14 | 14 | 14 | 14 | 14 | |
| 8 | De diámetro | Mm | 0.56+0.03 | 0.61+0.03 | 0.66+0.03 | 0.66+0.03 | 0.75+0.03 | 0.74+0.03 | 0.81+0.03 | |
| 9 | Twist | Pingle twist(Z) | T/10cm. | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 |
| Telas twist(S) | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 | |||
| 10 | El encogimiento de aire caliente a 177ºC×2minx0.05CN/dtex(máx.). | % | 2 | 2 | 2 | 2 | 2 | 2 | 2 | |
| 11 | @ De elongación de la rotura de hilo de trama (Min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 | |