C | Si | Mn | S | P | Ni | Nb+Ta |
≤0.1 | ≤0.5 | ≤0.5 | ≤ 0.015 | ≤0, 02 | ≥58.0 | 3.5-4.15 |
Al. | Ti | Fe | Cu | Cr | Mo | Otros |
≤0.4 | ≤0.4 | ≤5.0 | ≤0.5 | 20-23 | 8.0-10 | < 0, 5 |
C | Si | Mn | S | P | V | Ni |
≤0, 02 | ≤0, 08 | ≤1, 00 | ≤0, 03 | ≤0, 40 | 8.0-10.0 | Rem |
Fe | Cu | Co | Cr | Mo | W | Otros |
4.0-7.0 | ≤0, 50 | ≤2.5 | 14.5-16.5 | 15.0-17.0 | 3.0-4.5 | ≤0.5 |
El grado | Ni% | C% | Mn% | Fe% | S% | Cu% | Si% | Cr% | Ti% | Nb% | P% |
ERNiCr-3 | Min 67 | Max 0.05 | 2.5-3.5 | Max 3.0 | Máx. 0.015 | Max 0.50 | Max 0.50 | 18.0-22.0 | Max 0.75 | 2.0-3.0 | Máx. 0.015 |
Proceso | De diámetro | La tensión | El amperaje | El gas |
TIG | . 035" (0, 9 mm) . 045" (1.2mm) 1/16" (1.6mm) 3/32" (2, 4 mm) de 1/8" (3.2mm) | 12-15 13-16 14-18 15-20 15-20 | 60-90 80-110 90-130 120-175 150-220 | 100% 100% de Argón Argón 100% de Argón 100% de Argón 100% de argón |
MIG | . 035" (0, 9 mm) . 045" (1.2mm) 1/16" (1.6mm) | 26-29 28-32 29-33 | 150-190 180-220 200-250 | El 75%Argón+25%Helio El 75%Argón+25%Helio El 75% de Argón + 25% helio |
Vio | 3/32" (2, 4 mm) 1/8" (3.2mm) 5/32" (4, 0 mm) | 28-30 29-32 30-33 | 275-350 350-450 400-550 | Fundente adecuado Puede Ser Utilizado Tal vez fundente adecuado Usa Fundente adecuado puede ser utilizado |
Fuerza tensil | 86.000 PSI | 590 MPA |
Límite de fluencia | 52.000 PSI | 360 MPA |
La elongación | El 38% | |