| Categoría | HC90 | La HC92 | La HC95 | HCT95 | La HC99 | HC-ZTA | ZrO2 |
| Al2O3 | ≥90% | ≥92% | ≥95% | ≥95% | ≥ 99% | ≥75% | / |
| ZrO2 | / | / | / | / | / | ≥21% | ≥95% |
| Densidad | > 3, 50 g/cm3 | > 3, 60g/cm3 | > 3, 65g/cm3 | > 3.70g/cm3 | > 3.83g/cm3 | > 4.10g/cm3 | > 5.90g/cm3 |
| HV 20 | ≥900 | ≥950 | ≥1.000 | ≥1100 | ≥1200 | ≥1350 | ≥1100 |
| Dureza de la roca de la HRA | ≥80 | ≥82 | ≥85 | ≥88 | ≥90 | ≥90 | ≥88 |
| Resistencia a la flexión MPa | ≥180 | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 |
| Fuerza de compresión MPa | ≥970 | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / |
| Tenacidad de Fractura KIC MPam 1/2 | ≥3, 5 | ≥3, 7 | ≥3, 8 | ≥ 4.0 | ≥ 4.2. | ≥4, 5 | ≥ 7.0 |
| El volumen de desgaste | ≤0, 28 cm3 | ≤0, 25 cm3 | ≤0.20cm3 | ≤0, 15 cm3 | ≤0, 10 cm3 | ≤0, 05 cm3 | ≤0, 02 cm3 |