| Los grandes fabricantes | BAOSTEEL, WISCO, Nippon Steel, JFE, AK |
| El grado | CRGO: 20ZDKH75, B20P075, B20P070, B18R070. B23G110, B23G100, P100, B23B23R095, B23R090, 23zh90,23QG090, B23R080 27p120, 27 de QG100, 27 de QG095 B27P120, B27P100, B27P095 30p130, 30Q120, 30 QG105; b30G130, B30G120, B30P120, B30P105. 35p155, B35G155, 35Z155 |
| CRNGO: B35A270, B35A250, B35A230, B35A300, 35WW270,35250,35WW WW230 B50A800, B50A600, B50A470, B50A400, B50A310, B50A290, B50A250, B50A1300, B50A1000 | |
| Espesor nominal | 0,18 mm y 0.20mm 0,23mm,0,27 mm,0.30mm,0,35 mm, 0,5 mm |
| ID de la bobina | 508mm |
| El peso | 2MT~8MT |
| Standard | EN 10106, IEC 60404-8-4, ASTM, DIN,GB,JIS |
| Formulario | Bandas laminadas en frío |
| plazo de entrega entrega | 7~15 días después de T/T de prepago o L/C de la fecha |
| El embalaje | Paquete de exportación estándar para el transporte marítimo |
| Aplicación | Todo tipo de transformador, el reactor de filtro, el inversor, |
| Tipo | El grado | El grosor (mm) | Anchura disponible range(mm) | ID. | La densidad (kg/dm³) | P17/50Max.Core pérdida(W/kg). | B8Min.Inducción(T) |
| Tipo común | B23G110 | 0.23 | 700-1200 | 508 | 7.65 | 1.10 | 1.80 |
| B27G120. | 0.27 | 1.20 | 1.80 | ||||
| B30G120. | 0.30 | 1.20 | 1.80 | ||||
| B30G130 | 1.30 | 1.80 | |||||
| B30G140 | 1.40 | 1.80 | |||||
| B35G135 | 0.35 | 1.35 | 1.80 | ||||
| B35G145 | 1.45 | 1.80 | |||||
| B35G155 | 1.55 | 1.80 | |||||
| Tipo de inducción de alta | B23P090. | 0.23 | 0.90 | 1.87 | |||
| B23P095 | 0.95 | 1.87 | |||||
| B23P100 | 1.00 | 1.87 | |||||
| B27P095 | 0.27 | 0.95 | 1.88 | ||||
| B27P100 | 1.00 | 1.88 | |||||
| B27P110 | 1.10 | 1.88 | |||||
| B30P100 | 0.30 | 1.00 | 1.88 | ||||
| B30P105. | 1.05 | 1.88 | |||||
| B30P110 | 1.10 | 1.88 | |||||
| B30P120. | 1.20 | 1.88 | |||||
| B35P135 | 0.35 | 1.35 | 1.88 | ||||
| B35P155 | 1.55 | 1.88 | |||||
| Tipo de inducción de alta refinado de dominio | B23R080 | 0.23 | 0.80 | 1.87 | |||
| B23R085 | 0.85 | 1.87 | |||||
| B23R090. | 0.90 | 1.87 | |||||
| B27R090. | 0.27 | 0.90 | 1.87 | ||||
| B27R095 | 0.95 | 1.87 | |||||
| Nota: | |||||||
| La detección de base GB/T3655-2000 | |||||||
| P17/50 núcleo significa la pérdida de la muestra por kg en max.1.7T inducción magnética y la frecuencia 50Hz | |||||||
| B8 significa que la inducción magnética que corresponde a 800A/m de la intensidad de campo magnético | |||||||