El modelo | Tipo | 25ºC pa.s Viscosidad | Min Tiempo de gel | No volátil | MPa Fuerza tensil | La elongación | Fuerza de flexión MPa | HDT °C. |
191cc-G. | DC | 0.20-0.45 | 6.0-12.0 | 68-74 | 58 | 2.9 | 93 | 85 |
DC191 | DC | 0.20-0.45 | 6.0-12.0 | 68-74 | 58 | 2.9 | 93 | 85 |
191 | PA | 0.25-0.45 | 9.0-17.0 | 61-70 | 60 | 3.5 | 112 | 70 |
9196 | DC | 0.25-0.45 | 5.0-18.0 | 68-75 | 50 | 2 | 90 | 85 |
196 | PA | 0.25-0.45 | 9.0-17.0 | 61-67 | 60 | 1.8 | 113 | 66 |
196F | PA | 0.25-0.45 | 9.0-17.0 | 61-67 | 60 | 1.8 | 111 | 66 |
5118F | ISPA | 0,35-0,80 | 5.0-13.0 | 63-71 | 60 | 2.3. | 110 | 70 |
199 | ISPA | 0,35-0.65 | 10.0-16.0 | 56-64 | 55 | 1.8 | 90 | 120 |
199X | PA | 0,35-0.65 | 13.0-19.0 | 56-62 | 60 | 2 | 90 | 115. |
3301 | La ABPA | 0,35-0.58 | 5.8-10.7 | 56-62 | 55 | 2 | 105 | 100 |
197 | La ABPA | 0.40~0.50 | 10~25 | 47~53 | 60 | 2 | 90 | 115. |
El tema | Gama | Unidad | Método de ensayo |
Apariencia | Líquido viscoso de color amarillo claro | - | GB/T 8237.4.1.1 |
El valor de ácido | 25-30 | MgKOH/g | GB/T 2895 |
Viscosidad,25º C. | 0.25-0.45 | Pa.s | GB/T de 7193.1 |
Contenido de sólidos | 61-70 | % | GB/T de 7193.3 |
Tiempo de gel ,25º C. | 9-17 | Min | GB/T 7193-2008 |
El tema | Unidad | El valor medido | Método de ensayo |
La dureza de barco | -- | 41 | GB 3854-83 |
Temperatura de deformación térmica | °C. | 70 | GB 1634-04 |
Resistencia a la flexión | MPa | 112 | GB/T 2570-95 |
Fuerza tensil | MPa | 60 | GB/T 2568-95 |
Alargamiento de rotura | % | 3.5 | GB/T 2568-95 |
La resistencia al impacto | KJ/m2 | 10.2 | GB/T 2571-95 |
El tema | Unidad | Los datos medidos | Método de ensayo |
Resistencia a la flexión | MPa | 365 | GB/T1449-83 |
Fuerza tensil | MPa | 290 | GB/T1447-83 |