Place of Origin: | China |
Refinement: | Fully Refined |
Forms: | Solid |
Color: | white |
Melting Point: | 58-66ºC |
Crystalline Index: | 99.% |
Scale of Deoiling: | 99% |
Oil Content (%): | 0.5 |
Grades | HDPE PN049 | HDPE-100 | HDPE-80 | HDPE-6081H | HDPE-3000JE |
(5.0kg,190ºC)Melt mass-flow rate ,g/10min | 0.26 | 0.26 | 0.430 | 6.22 | 2.2 |
Density,g/cm³ | 0.95 | 0.95 | 0.9458 | 0.9577 | 0.956 |
Tensile stress at yield,Mpa | 23.3 | 23.3 | 21.3 | 26.1 | 24.8 |
Modulus of elasticity in tension,Mpa | 882 | 882 | - | - | - |
Flexural modulus,Mpa | 1047 | 1047 | 955 | 1057 | 1020 |
23ºC Charpy impact strength,KJ/m² | 37.8 | 37.8 | 11.8H | 4.2 | 12 |
Temperature of deflection under load(Tf0.45),ºC | 77 | 77 | - | - | 68 |
Water content,mg/kg | 14 | 14 | 58 | - | - |
Volatile content,mg/kg | 213 | 213 | 112 | - | - |
0xidation induction time(0IT,210ºC),min | 78.3 | 78.3 | 28.9 | - | - |
Nominal tensile strain at break,% | 560 | 560 | 298 | 661 | 9.6 |
Application | drain pipe | drain pipe | Water pipe | Injection bottle cap | Injection bottle cap |
Grades | HDPE-32F | HDPE-B507 | HDPE-B502 | HDPE-XP9020 | HDPE-6098 |
(5.0kg,190ºC)Melt mass-flow rate,g/10min | 1.98 | 6.43 | 1.86 | 0.14 | 0.38 |
Density,g/cm³ | 0.9373 | 0.948 | 0.9507 | 0.941 | 0.9494 |
Tensile stress at yield,Mpa | 16.8 | 21.7 | 23.6 | 220 | 22.5 |
Modulus of elasticity in tension,Mpa | - | - | 969 | - | - |
Flexural modulus,Mpa | 741 | - | - | 6200 | - |
23ºC Charpy impact strength,KJ/m² | 28.6P | - | 43.1P | - | - |
Temperature of deflection under load(Tf0.45),ºC | 127.2 | - | - | - | - |
Water content,mg/kg | 22 | - | - | - | - |
0xidation induction time(0IT,210ºC),min | 65.7 | - | - | - | - |
Nominal tensile strain at break,% | 869 | 850 | 774 | >600 | 466 |
Application | PEX-A floor heating pipe | various types of bottles, cans and industrial tanks and barrels | various types of bottles, cans and industrial tanks and barrels | Floor heating pipe | Shopping bag,market bag,garbage bag,drain pipe,etc. |
Grades | HDPE-TR400N | HDPE-YEC-5505T | HDPE-5000S | HDPE-1158 | HD6007XA | HDPE-QHJ01 |
(5.0kg,190ºC)Melt mass-flow rate,g/10min | 11.6(21.6kg) | 0.7 | 1.0 | 2.1 | 0.6 | 0.7 |
Density,g/cm³ | 0.939 | 0.945 | 0.951 | 0.953 | 0.962 | 0.945 |
Tensile stress at yield,Mpa | 20 | 19 | 25 | 24 | 30.5 | 18 |
Flexural modulus,Mpa | - | - | - | - | 1700 | 9 |
23ºC Charpy impact strength,KJ/m² | - | - | - | 32 | - | - |
Nominal tensile strain at break,% | 799 | 500 | 800 | 600 | 300 | 500 |
Application | Blow molding geomembrane products | Base Resin of Chlorinated PolyethyleneBase Resin of Chlorinated Polyethylene | Package film, nets, ropes and small and medium-sized containers | Blow Molding Grade | Blow Molding Grade | Cable and wire |