| Nom de la classe | Qualité normale CA50 | ||||
| Saisissez No. | X5 | X6 | X7 | ||
| Chimique Composant | SiO2 | ≤8 | ≤8 | ≤7.5 | |
| Al2O3 | ≥ 50.0 | ≥ 50.0 | ≥ 52.0 | ||
| Fe2O3 | ≤2.5 | ≤2.5 | ≤2.0 | ||
| R2O | ≤0.4 | ≤0.4 | ≤0.4 | ||
| Phase principale du cristal | ENV | ||||
| Phase secondaire | CA2,C12A7,C2AS,CT | ||||
| Résidus après 325 mesh (%) | ≤15 | ||||
| Blaine (m2/kg) | ≥ 300 | ||||
| Temps de réglage initial (min) | ≥ 30 | ||||
| Heure de réglage final (h) | ≤6 | ||||
| Résistance à la flexion (MPa) | 1d | 5.5 | 6 | 6.5 | |
| 3d | 6.5 | 7 | 7.5 | ||
| Résistance à la compression (MPa) | 1d | 40 | 45 | 50 | |
| 3d | 50 | 55 | 60 | ||
| Nom de la classe | CA50 haute résistance | ||||||
| Saisissez No. | X9 | N | PROTÉGÉ PAR FUSIBLE | ||||
| Chimique Composant | SiO2 | ≤7.0 | ≤7.0 | ≤6.0 | |||
| Al2O3 | ≥ 55.0 | ≥ 55.0 | ≥ 55.0 | ||||
| Fe2O3 | ≤2.5 | ≤2.5 | ≤2.5 | ||||
| R2O | ≤0.4 | ≤0.4 | ≤0.4 | ||||
| Phase principale du cristal | ENV | ||||||
| Phase secondaire | CA2, C2AS | C12A7, C2AS | C12A7, C2AS | ||||
| Résidus après 325 mesh (%) | ≤15 | ||||||
| Blaine (m2/kg) | ≥ 400 | ≥ 350 | ≥ 400 | ||||
| Temps de réglage initial (min) | ≥ 90 | ≥ 30 | ≥ 120 | ||||
| Heure de réglage final (h) | ≤6 | ≤6 | ≤8 | ||||
| Résistance à la flexion (MPa) | 6-8h | - | 4 | 4 | |||
| 1d | 8 | 6 | 10 | ||||
| 3d | 10 | 7 | 11 | ||||
| Résistance à la compression (MPa) | 6-8h | - | 30 | 30 | |||
| 1d | 70 | 50 | 75 | ||||
| 3d | 80 | 60 | 80 | ||||