Film rétractable POF | |||||||
ITEM DE TEST | UNITÉ | TEST ASTM | VALEURS TYPIQUES | ||||
ÉPAISSEUR | 12 microns | 15 microns | 19 microns | 25 microns | 30 microns | ||
RÉSISTANCE À LA TRACTION | N/mm2 | D882 | MD TD | MD TD | MD TD | MD TD | MD TD |
115 110 | 110 105 | 110105 | 100 95 | 90 85 | |||
ALLONGEMENT | % | D882 | 120 110 | 120 115 | 125 120 | 130 125 | 130 125 |
DÉCHIRURE | g | D1992 | 11.5 11.0 | 11.0 13.5 | 17.5 17.0 | 24.0 23.5 | 28.0 27.0 |
RÉSISTANCE À LA SOUDURE | N/mm | F88 | 0.68 /0.70 | 0.80/0.85 | 1.00/1.05 | 1.27/1.30 | 1.50/1.55 |
COF DYNAMIQUE | D1894 | 0.22 | 0.23 | 0.24 | 0.24 | 0.25 | |
TROUBLE | D1003 | 2.10 | 2.60 | 3.00 | 3.80 | 4.40 | |
CLARTÉ | D1746 | 99.0 | 98.0 | 97.0 | 95.0 | 92.0 | |
BRILLANCE | D2457 | 85.0 | 87.0 | 83.5 | 82.5 | 80.0 | |
RÉTRACTION À 100ºC | % | D2732 | 23 | 31 | 21 | 27 | |
RÉTRACTION À 110ºC | % | D2732 | 38 | 40 | 35 | 39 | |
RÉTRACTION À 120ºC | % | D2732 | 57 | 60 | 56 | 61 | |
RÉTRACTION À 130ºC | % | D2732 | 65 | 67 | 64 | 65 | |
TENSION DE RÉTRACTION | Mpa | D2838 | MD | TD | MD | TD | |
100ºC | 1.85 | 2.60 | 1.80 | 2.55 | |||
110ºC | 2.75 | 3.50 | 2.70 | 3.60 | |||
120ºC | 2.80 | 3.65 | 2.80 | 3.65 | |||
130ºC | 2.65 | 3.25 | 2.60 | 3.15 |