Complaint
| Le point | 1870dtex/2 (1680D/2) | 1400dtex/2 1260D/2 | 930dtex/2 840D/2 | 2100dtex/2 (1890d/2) | 1170dtex/1 (1050D/1) | 700dtex/1 (630D/1) | 1870dtex/1 (1680D/1) | 1400dtex/1 (1260D/1) | 930dtex/1 (840D/1) | ||
| Résistance à la rupture≥ | N/fin | 279.30 | 215.60 | 137.20 | 313.60 | 90.00 | 50.00 | 137.00 | 107.00 | 70.00 | |
| Allongement à la | 88.2N | % | 9,5±0,5 | - | - | 9,5±0,5 | - | - | 8,0±0,8 | - | - |
| 66.6N | - | 9,5±0,5 | - | - | 8,0±0,8 | - | - | 7.0±0.8 | - | ||
| 44.1N | - | - | 9,5±0,5 | - | - | 7,5±0,8 | - | - | 7,5±0,8 | ||
| Résistance adhésive≥ | N/cm | 166.60 | 147.00 | 117.60 | 176.40 | 65.00 | 43.00 | 83.00 | 69.00 | 54.00 | |
| Résistance à la rupture différence≤ | % | 3.80 | 3.80 | 3.80 | 3.80 | 5.00 | 5.00 | 5.00 | 5.00 | 5.00 | |
| L'allongement de rupture différence≤ | 6.30 | 6.30 | 6.30 | 6.30 | 7.00 | 7.50 | 7.00 | 7.00 | 7.00 | ||
| Ramasser dip | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | ||
| L'allongement de rupture | % | 23,0±2,0 | 23,0±2,0 | 22,0±2,0 | 23±2.0 | 20,0±2,0 | 19,0±2,0 | 20,0±2,0 | 20,0±2,0 | 20,0±2,0 | |
| Diamètre | Mm | 0,78±0,03 | 0,65±0,03 | 0,55±0,03 | 0,78±0,03 | - | 0,23±0,03 | 0,5±0,03 | 0,43±0,03 | 0,32±0,03 | |
| Twist | Twist primaire(Z) | Twist/m | 320±15 | 370±15 | 460±15 | 320±15 | Le module TPM/m : 200±15 | Le module TPM/m : 260±15 | 160±10 | 190±10 | 210±15 |
| Deuxième twist(S) | 320±15 | 370±15 | 460±15 | 320±15 | |||||||
| Le rétrécissement thermique ≤ | % | 6.00 | 6.00 | 6.00 | 4.00 | 4.50 | 4.00 | 4.00 | 4.00 | 4.00 | |
| L'humidité ≤ | % | 1.00 | 1.00 | 1.00 | 1.00 | 0.80 | 0.80 | 0.80 | 0.80 | 0.80 | |
| NO. | Les articles | UNITE | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
| (1100dtex/2) | (1440 dtex/2) | (1100dtex/3) | (1670dtex/2) | (2200dtex/2) | (1440 dtex/3) | (1670dtex/3) | ||||
| 1 | Breaking Stength (min) | N/fin | 140 | 180 | 205 | 205 | 280 | 260 | 305 | |
| 2 | Allongement à 44,1N | % | 4.5+1.0 | |||||||
| Allongement à 58.0N | % | 4.5+1.0 | ||||||||
| Allongement à 66.6N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Allongement à 88.2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Allongement à la 100N | % | 4.5+1.0 | ||||||||
| 3 | Adhension(H-test)(min) | N/cm | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
| 4 | Résistance à la rupture Différence(max) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| 5 | L'allongement de rupture Différence(max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 6 | Ramasser dip | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
| 7 | L'allongement de rupture (min). | % | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | |
| 8 | Diamètre | Mm | 0,56+0.03 | 0,61+0.03 | 0,66+0.03 | 0,66+0.03 | 0,75+0.03 | 0,74+0.03 | 0,81+0.03 | |
| 9 | Twist | Pingle twist(Z) | T/10cm | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 |
| Ply twist(S) | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 | |||
| 10 | Le rétrécissement de l'air chaud 177ºC×2minx0,05CN/dtex(max) | % | 3 | 3 | 3 | 3 | 3 | 3 | 3 | |
| 11 | L'élongation @ rupture de fils de trame (min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 | |
| NO. | Les articles | UNITE | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
| (1100dtex/2) | (1440 dtex/2) | (1100dtex/3) | (1670dtex/2) | (2200dtex/2) | (1440 dtex/3) | (1670dtex/3) | ||||
| 1 | Breaking Stength (min) | N/fin | 140 | 180 | 205 | 205 | 270 | 260 | 305 | |
| 2 | Allongement à 44,1N | % | 4.5+1.0 | |||||||
| Allongement à 58.0N | 4.5+1.0 | |||||||||
| Allongement à 66.6N | 4.5+1.0 | 4.5+1.0 | ||||||||
| Allongement à 88.2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Allongement à la 100N | % | 4.5+1.0 | ||||||||
| 3 | Adhension(H-test)(min) | N/cm | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
| 4 | Résistance à la rupture Différence(max) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| 5 | L'allongement de rupture Différence(max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 6 | Ramasser dip | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
| 7 | L'allongement de rupture (min) | % | 14 | 14 | 14 | 14 | 14 | 14 | 14 | |
| 8 | Diamètre | Mm | 0,56+0.03 | 0,61+0.03 | 0,66+0.03 | 0,66+0.03 | 0,75+0.03 | 0,74+0.03 | 0,81+0.03 | |
| 9 | Twist | Pingle twist(Z) | T/10cm | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 |
| Ply twist(S) | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 | |||
| 10 | Le rétrécissement de l'air chaud 177ºC×2minx0,05CN/dtex(max) | % | 2 | 2 | 2 | 2 | 2 | 2 | 2 | |
| 11 | L'élongation @ rupture de fils de trame (min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 | |