درجات من الفولاذ المقاوم للصدأ |
النوع | الدرجة | الدرجة | المكون الكيميائي % |
ج | CR | نيكل | MN | P | س | الاثنين | SI | وحدة | n | غير ذلك |
التضييق | 201 | SUS201 | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
202 | SUS202 | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | | ≤1.00 | - | ≤0.25 | - |
301 | 1.4310 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - |
302 | 1Cr18Ni9 | ≤0.15 | 17.00-19.00 | من 8.00 إلى 10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - |
303 | 1.4305 | ≤0.15 | 17.00-19.00 | من 8.00 إلى 10.00 | ≤2.00 | ≤0.20 | ≤0.030 | - | ≤1.00 | - | - | - |
303se | Y1C18Ni9Se | ≤0.15 | 17.00-19.00 | من 8.00 إلى 10.00 | ≤2.00 | ≤0.20 | ≤0.030 | - | ≤1.00 | - | - | SE 0.15 |
304 | 1.4301 | ≤0.07 | 17.00-19.00 | من 8.00 إلى 10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
304 لتر | 1.4307 | ≤0.030 | 18.00-20.00 | من 8.00 إلى 10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | من 8.00 إلى 10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
305 | * | ≤0.12 | 17.00-19.00 | 11.00-13.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
308 | * | ≤0.08 | 19.00-21.00 | 10.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
309 | 1.4828 | ≤0.20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
309S | * | ≤0.08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - |
310 | 1.4842 | ≤0.25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - |
310S | * | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - |
314 | 1.4841 | ≤0.25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - |
316 | 1.4401 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - |
316 لترًا | 1.4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - |
316Ti | 1.4571 | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0.70 |
317 | * | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - |
317L | 1.4438 | ≤0.03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - |
321 | 1.4541 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 |
321H | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 |
347 | 1.4550 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | ملاحظة: ≥ 10*C%-1.10 |
347H | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | ملاحظة: ≥ 10*C%-1.10 |
XM-19 | نيترونيك50 | ≤0.06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0.045 | ≤0.030 | 1.50-3.00 | ≤1.00 | - | 0.2-0.4 | ملاحظة: 0.10-0.30 فولت:0.10-0.30 |
4L | N08904 | ≤0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0.045 | ≤0.035 | | ≤1.00 | | 0.1 | Cu:1.0-2.0 |
الطباعة على الوجهين | 2205 | S32205 | ≤0.03 | 22.0-23.0 | 4.5-6.5 | ≤2.00 | ≤0.030 | ≤0.020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
2507 | S32750 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0-5.0 | ≤0.80 | 0.5 | 0.24-0.32 | |
* | S32760 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.00 | ≤0.030 | ≤0.010 | 3.0-4.0 | ≤1.00 | 0.5-1.00 | 0.2-0.3 | |
2304 | S32304 | ≤0.03 | 21.5-24.5 | 3.0-5.5 | ≤2.50 | ≤0.040 | ≤0.030 | 0.05-0.6 | ≤1.00 | 0.05-0.6 | 0.05-0.2 | |
329 | 1.4460 | ≤0.08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0.75 | - | - | |
الفرّيت | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)~0.50 NB:0.17 |
430 | 1C17 | ≤0.12 | 16.00-18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - |
430F | Y1C17 | ≤0.12 | 16.00-18.00 | - | ≤1.25 | ≤0.060 | ≥0,15 | - | ≤1.00 | - | - | - |
444 | S44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | ≤1.00 | - | 0.035 | TI+NB:0.2+4(C+N)~0.80 |
446 | S44600 | ≤0.20 | 23.00-27.00 | 0.75 | ≤1.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | ≤1.00 | - | ≤0.25 | - |
مارتنست | 410 | 1C13 | 0.08-0.15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
416 | Y1C13 | ≤0.15 | 12.00-14.00 | 3) | ≤1.25 | ≤0.060 | ≥0,15 | - | ≤1.00 | - | - | - |
420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
420J2 | 3C13 | 0.26-0.35 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
420F | Y3Cr13 | 0.30-0.40 | 12.00-14.00 | 0.5 | ≤1.25 | ≤0.060 | ≥0,15 | - | ≤1.00 | 0.6 | - | - |
* | 4C13 | 0.36-0.45 | 12.00-14.00 | 3) | ≤0.80 | ≤0.040 | ≤0.030 | - | ≤0.60 | - | - | - |
431 | 1C17Ni2 | ≤0.20 | 15.00-17.00 | 1.50-2.50 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤0.80 | - | - | - |
440C | 11C17 | 0.95-1.20 | 16.00-18.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | 0.75 | ≤1.00 | - | - | - |
الرقم الهيدروجيني (p | 630 | 17-4PH | ≤0.07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | NB 0.15-0.45 |
631 | 17-7PH | ≤0.09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | Al 0.75-1.50 |
632 | 15-5PH | ≤0.09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0.75-1.50 |