Self Adhesive Decorative PVC Metalized Film

self adhesive decorative pvc metalized film




Products:
1. Aluminum metallized polypropylene film.
2.Aluminum metallized polypropylene safety film.
3.Zinc - Aluminum alloy metallized polypropylene film with heavy edge.
4. Zinc - Aluminum alloy metallized polypropylene safety film with heavy edge.
5.Zinc - Aluminum alloy metallized polypropylene film with heavy edge and slope metallized film.
6.Aluminum metallized polyester film.
7.Zinc - Aluminum alloy metallized polyester film with heavy edge.
8.Zinc-Aluminum Alloy metallized polypropylene film with high ssquare resistance
9. According to customer requirement design to producing all kinds of metallized film for capacitor used.

Cores:
1.Material:Plastic.
2.Width:Film Slit Width ±0.3mm.
3.Inner Diameter:75mm +1.0mm/-0.5mm.

Roll Outer Diameter:

Slit widths(W)
Recommend outer diameter(D)
4.5mm≤W<10mm
140mm≤D≤185mm
10mm≤W<25mm
150mm≤D≤185mm
25mm≤W<50mm
150mm≤D≤240mm
50mm≤W
150mm≤D≤350mm

Specifications of metallized film:
1)Metallized polypropylene film


Properties

Unit

Requirements
Density
g/cm3
0.905±0.005
Thickness
µm
3.8 ~ 15

Tensile Strength
MD
(MPa)
≥100

Elongation at Break
MD
(%)
40 ~ 200

Heat Shrinkage
MD
(%)
≤5 ( 120°C, 10min)
( 120°C , 10 min )

Break-dowm voltage
V/µm
≥350 ( 23°C, DC )

Coating square resistance
Al
1.5±0.5
2.0±0.5
2.5±0.5
3±1

Zn/Al
(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%
with gradient square
(heavy-edge area):3±1
(non heavy-edge area):(2~20)

Dissipation Factor
-
≤4×10-4 (20ºC,1KHz )
RC
ΩF
≥5×104

2.)Metallized polyester Film


Properties

Unit

Requirements
Density
g/cm3
1.34
Thickness
µm
<5
5~12
>12

Tensile Strength
MD
(MPa)
≥84
≥108
≥120

Elongation at Break
MD
(%)
≥22
≥33
≥44

Break-dowm voltage
V/µm
≥200
( 23°C, DC )
≥250
( 23°C, DC )

Heat Shrinkage
MD
(%)
≤3 ( 120°C, 10min)

Coating square resistance
Al
1.5±0.5
2.0±0.5
2.5±0.5
3±1

Zn/Al
(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%

Dissipation Factor
-
≤60×10-4 (20ºC,1KHz )
RC
ΩF
≥1×104

Note: Coating square resistance annotation is a typical value,can be customized.

Packing:
1. Roll films are packed in vacuum plastic bag and heat-sealed with desiccants.
2.Bags are marked with lables of types
3. The bags are packed in carton cases.
4.The cartons are wrapped in wooden cases or reinforced carton.


Storge:
1. Metallized film should be stored in its original package until its use with temperature 5 ~ 35ºC and humidity less than 85%RH.
2. Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.

3.The recommended temperature is 15 -25ºC with humidity less than 60%RH after the package is open.

4.With original sealed package, and stored in the above mentioned conditions, the storage time can be as following:
Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period(from delivery date) depends on the resistance of the film:
≤10 Ω/: 6 months
10 ~15Ω/: 3 months
>15Ω/: 1months