Flame Retardant Heat Conducting Nylon 66 Polyamine PA 66 Epoxy Resin
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| General | ||
| Form Resin Pellets | ||
| Feature Anti-Static Electrically Conductive Thermally Conductive | ||
| Physical | Nominal Value | Test Method |
| Density / Specific Gravity | 1.80 g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Test Method |
| Tensile Strength, Break | 55.2 MPa | ASTM D638 |
| Elongation at Break | < = 1.0 % | ASTM D638 |
| Tensile Modulus | 2.07E+4 MPa | ASTM D638 |
| Flexural Strength | 89.6 MPa | ASTM D790 |
| Flexural Modulus | 2.07E+4 MPa | ASTM D790 |
| Izod Impact, Notched(Thickness; 3.2 mm) | 26.7 J/m | ASTM D256 |
| Izod Impact, Unnotched(Thickness; 3.2 mm) | 80.1 J/m | ASTM D4812 |
| Thermal | Nominal Value | Test Method |
| Thermal conductivity through plane(through-plane) | 3.002 W/m-K | ASTM E1530 |
| Thermal conductivity in plane(in-plane) | 20.013 W/m-K | ASTM E1461 |
| Flammability, UL94(Thickness; 1.5 mm) | V-0 | UL 94 |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | < = 100 ohms ·cm | ASTM D257 |
| Surface Resistivity per Square | < = 10000 Ohms | ASTM D257 |
| Processing | Nominal Value | |
| Melt Temperature | 277 - 299 °C | |
| Mold Temperature | 79.4 - 121 °C | |
| Drying Temperature(Time 4 hr) | 79.4 °C | |
| Moisture Content | 0.20 % | |
| Dew Point | -17.8 °C | |
| Injection Pressure | 68.9 - 124 MPa | |