Product Description | ||||
CX7110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable, high flow, non chlorinated/brominated flame retardant grade. It has a UL94 [email protected] and [email protected] flame rating. This grade has improved chemical resistance compared to standard PC/ABS blends and is a good candidate for thin wall applications. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Chemical Resistant Non-Chlorinated | Excellent Processability Thin Wall | Non-Brominated & Non- Chlorinated Flame Retardant | |
UL Yellow Card | E121562-566198 E207780-566196 E45329 566194 | |||
Uses Consumer | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.19 1.19 g/cm³ | ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.6 % | SABIC Method | ||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 22 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.2 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | ||
Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C) | 21 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched 23 °C -30 °C | 600 J/m 120 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 63 J | ASTM D3763 | ||
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 15 kJ/m² 10 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | 15 kJ/m² 10 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 64 MPa | ASTM D638 |
50 mm/min | 61 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 54 MPa | ASTM D638 |
50 mm/min | 51 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 4 % | ASTM D638 |
50 mm/min | 4 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 90 % | ASTM D638 |
50 mm/min | 90 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2900 MPa | ASTM D638 |
1 mm/min | 2700 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 100 MPa | ASTM D790 |
2 mm/min | 100 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2700 MPa | ASTM D790 |
2 mm/min | 2500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 1.8 mm ≥ 1.2 mm ≥ 1 mm ≥ 0.75 mm | 5VB V-0 V-1 V-2 | UL 94 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 102 °C 102 °C 103 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm | 94 °C 84 °C 98 °C 90 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C | 7.5e-05 1/°C 7.5e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C | 7.5e-05 1/°C 7.5e-05 1/°C | ASTM E831 ISO 11359-2 |
Thermal Conductivity | 0.2 W/m-K | ISO 8302 |
Ball Pressure Test(75°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Af(1.8) | 84 °C | ISO 75/Af |
Relative Temp Index, Elec | 90 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 90 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 90 °C | UL 746B |
Processing | Nominal Value |
Drying Temperature<Injection> | 80 - 90 °C |
Drying Time<Injection> | 3 - 4 hrs |
Drying Time, Cumulative<Injection> | 8 hrs |
Maximum Moisture Content<Injection> | 0.04 % |
Melt Temperature<Injection> | 245 - 275 °C |
Nozzle Temperature<Injection> | 245 - 275 °C |
Front, Zone 3 Temperature<Injection> | 245 - 275 °C |
Middle, Zone 2 Temperature<Injection> | 220 - 265 °C |
Rear, Zone 1 Temperature<Injection> | 220 - 255 °C |
Mold Temperature<Injection> | 60 - 80 °C |
Back Pressure<Injection> | 0.3 - 0.7 MPa |
Screw Speed <Injection> | 40 - 70 rpm |
Shot To Cylinder Size<Injection> | 30 - 80 % |
Vent Depth <Injection> | 0.038 - 0.076 mm |