| Product Description | Applications |
·10%,20%6
10% glass fiber reinforced,20% mineral filled PA6 | · Injection molding |
| · Excellent heat stability | · Good mechanical properties balance |
| Properties | Test Method | Test Condition | Unit | Typical Values |
| Physical properties |
| Specific Gravity | ISO 1183 | 23ºC | g/cm3 | 1.35 |
| Ash | ISO 3451 | 800ºC,30min | % | 30 |
| Mechanical properties |
| Tensile Strength | ISO 527 | 50mm/min | MPa | 125 |
| Elongation at Break | ISO 527 | 50mm/min | % | 2.5 |
| Flexural Modulus | ISO 178 | 2mm/min | MPa | 8500 |
| Izod Notched Impact Strength | ISO 180 | 23ºC | kJ/m2 | 9 |
| Thermal properties |
| Heat deflection temperature | ISO 75 | 1.80MPa | C | 185 |
| Melting Point | DSC | - | C | 222 |
| Other properties |
| Mold Shrinkage | internal test method | 48 hours after tool | % | 0.3-0.5 |
| Flammability | TL1010 | - | mm/min | 39 |
| Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type , gate location, gate number, injection molding process and part thickness. The data will vary with different color as well. Prior to use the material, please consult with Sunway polymer. |
| Processing Conditions | Range |
| Melt Temperature | 240-270ºC |
| Barrel Temperature | Rear | 240--250ºC |
| Center | 255--265ºC |
| Front | 260--270ºC |
| Mold Temperature | 50-80ºC |
| Pre-Dry needed | 100ºC, 4-8h |
| Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines, mold design and product design. |