Virgin Polycarbonate PC Copolymer Resin for Waterproof LED Profile Shape Channel
https://forever-plastics.en.made-in-china.com/product-list-1.html
Forever Co.,Ltd
Physical Property Value Condition | ||||
Density / Specific Gravity | 1.20 g/cm³ | 23°C | ASTM D792 | |
Melt Mass-Flow Rate, MFR | 22 g/10min | 300°C,1.2 kg | ASTMD1238 | |
Rockwell Hardness, M-Scale | 77 | ASTM D785 | ||
Mechanical Property Value Condition Standard | ||||
Tensile Strength, Yield | 61.6 MPa | 6 mm/min | ASTM D638 | |
Tensile Elongation, Break | 110% | 6 mm/min | ASTM D638 | |
Flexural Strength | 89.8 MPa | 1.3 mm/min | ASTM D790 | |
Notched Izod Impact | 820 J/m | 23 °C 3.2 mm | ASTM D256 | |
Thermal Property Value Condition Standard | ||||
Deflection Temperature Under Load, Annealed | 144 °C | 0.45 MPa 132 °C x 8 hr | ASTM D648 | |
Flame Rating | V-2 | 0.38 mm | UL94 | |
Flame Rating | V-2 | 3.2 mm | UL94 | |
Processing Property Value Condition | ||||
Drying Temperature | 120 °C | |||
Drying Time | 4.0hr | |||
High Amp Arc Ignition, HAI | PLC 0 | UL 746 | ||
High Voltage Arc Tracking Rate,HVTR | 80.0 - 150mm/min | UL 746 | ||
High Voltage Arc Tracking Rate,HVTR | PLC 3 | UL 746 | ||
Hot-wire Ignition,HWI | 30-60 sec | UL 746 | ||
Hot-wire Ignition,HWI | PLC 2 | UL 746 | ||
Thermal Property | Value Condition | |||
HDT, Unannealed | 135 °C | 1.8 MPa | ASTM D648 | |
RTI Elec | 125 °C | UL 746 | ||
RTI Imp | 115 °C | UL 746 | ||
RTI Str | 125 °C | UL 746 | ||
FlameRating | V-0 | 3 mm | UL94 | |
Processing Property Value Condition | ||||
Drying Temperature | 121 °C | |||
Drying Time | 3.0 - 4.0hr | |||