Complaint
| No. | Spec Item | EP-80 | EP-100 | EP-125 | EP-150 | EP-200 | EP-250 | EP-300 | EP-350 | EP-400 | ||||||||||
| unit | warp | weft | warp | weft | warp | weft | warp | weft | warp | weft | warp | weft | warp | weft | warp | weft | warp | weft | ||
| 1 | Frame | dtex | 1100X1 | 930X1 | 1100X1 | 930X1 | 1670X1 | 1400X1 | 1100X2 | 1870X1 | 1100X2 | 1400X2 | 1100X4 | 1870X2 | 1100 X4 | 1870 X2 | 1870 X3 | 1870 X2 | 1870X4 | 1870X2 |
| 2 | Density | radical /10cm | 155 ±2 | 76 ±2 | 194 ±2 | 86 ±2 | 170 ±2 | 72 ±2 | 166 ±2 | 56 ±2 | 186 ±2 | 44 ±2 | 120 ±2 | 38 ±2 | 146 ±2 | 38 ±2 | 150 ±2 | 38 ±2 | 125 ±2 | 38 ±2 |
| 3 | Average breaking strength≥ | N/mm | 100 | 50 | 137 | 55 | 165 | 70 | 206 | 75 | 246 | 85 | 330 | 105 | 350 | 105 | 400 | 105 | 465 | 105 |
| Breaking strength(min)≥ | 95 | 45 | 118 | 50 | 145 | 60 | 176 | 68 | 220 | 75 | 290 | 95 | 320 | 95 | 370 | 95 | 425 | 95 | ||
| 4 | Elongation at 10% load≤ | % | 1.5 | 15 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | |||||||||
| 5 | Elongation at break | % | ≥14 | ≥14 | ≤45 | ≥14 | ≤45 | ≥14 | ≤45 | ≤45 | ≥15 | ≤45 | ≥15 | ≤45 | ≥15 | ≤45 | ≥15 | ≤45 | ||
| 6 | Drying shrinkage %≤(150ºC*30min) | % | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 6.0 | 0.5 |
| 7 | Uneven drying shrinkage≤ | % | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | |||||||||
| 8 | Adhesion strength≥ | N/mm | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | |||||||||
| 9 | Weight (grams per m2) | g/m2 | 300±10 | 340±15 | 425±20 | 530±20 | 615±20 | 780±30 | 860±30 | 1000±35 | 1040±40 | |||||||||
| 10 | Thickness | mm | 0.55±0.05 | 0.55±0.05 | 0.60±0.05 | 0.70±0.05 | 0.80±0.05 | 1.07±0.10 | 1.20±0.10 | 1.26±0.10 | 1.40±0.10 | |||||||||
| 11 | Width | mm | 0 0 800~1400 -20 -20 | 0 0 800~1500 -20 -20 | 0 0 800~1500 -20 -20 | 0 0 800~1550 -20 -20 | 0 0 800~1600 -20 -20 ---- | 0 0 800~1600 -20 -20 | 0 0 800~1600 -20 -20 | 0 0 800~1600 -20 -20 | 0 0 800~1600 -20 -20 | |||||||||